Abstract:To further clarify the effect mechanism of MoS 2 element diffusion on tribological properties of cemented carbide materials, an investigation was carried in this study. The diffusion process between cemented carbide inserts and MoS 2 powder under high temperature condition was carried out in a muffle furnace device. The surface morphology and chemical element content of test samples were observed and measured with scanning electron microscope, energy spectrum, and X-ray diffraction instruments. The kinetics of the diffusion process was quantitatively discussed by thermodynamic experiments. Tribological experiments were carried out using friction and wear machine with which the friction coefficient and wear scar were obtained. The experimental results show that high temperature has a significant effect on physical and mechanical properties of cemented carbide materials. Moreover, MoS 2 elements diffusion on sample surface is existed and induced by thermal action, which results in a further changing of material properties of cemented carbide. The WC grain growth is inhibited when molybdenum element is only infiltration on sample surface at 500 °C, which improves the surface morphology and hardness of test sample. However, the oxidation rate, friction coefficient, and wear rate of test sample are the highest when heating temperature larger than 500 °C. The main reason is that, as the temperature increasing, the diffusion of sulfur elements is occurred and intensified the loss of cobalt element on sample surface. So, the bonding ability of it is decreased due to the loss of bonding phase Co. Thus, the surface hardness and wear resistance of test sample is deteriorated. This study provides a theoretical foundation for the application of molybdenum disulfide in tool cutting lubrication condition.

Study on the adhering failure mechanism of cemented carbide inserts and element diffusion model during the heavy-duty cutting of water chamber head

Adhering Failure and Optimization of Cemented Carbide Inserts for the Heavy-Duty Cutting of High-Strength Steel Forgings

Finite Element Simulation Of High-Speed Cutting Alloy Cast Iron

Simulation of Chip Formation in High-Speed Hard Machining

Analysis of Fatigue Damage of Cemented Carbide Insert During the Heavy-Duty Milling of Water Chamber Head

Design for Manufacturing of Cemented Carbide Coated Components Toward High Wear and Impact Resistance Performance

High-temperature mechanical properties of a cemented carbide cutter during extra-heavy cutting process

Wear Mechanisms of Cemented Carbide Tools in Dry Cutting of Precipitation Hardening Semi-Austenitic Stainless Steels

Analysis of High Temperature Wear Process Mechanism of Cemented Carbide Tool

Research on Cutting Temperature Distribution of Carbide Cutter Rake Face Considering Sticking-Welding Layer

Microstructural Evolution and Mechanical Properties of Diffusion Bonding WC-Co Cemented Carbide to Steel Using Co and Composite Ni/Co Interlayers

Cutting Performances and the Related Characteristics of CVD Coated Hardmetal Inserts Changed by Post-Treatments

Tool Life and Wear of WC–TiC–Co Ultrafine Cemented Carbide During Dry Cutting of AISI H13 Steel

3D Finite Element Simulation on High-speed Dry Hard Turning Process and Experiment Analysis

Effect of Nickel Element Diffusion on the Tribological Properties of Cemented Carbide Materials under High Temperature Condition

Influence of different wet-blasting pressure on the surface integrity and tool cutting performance of hybrid CVD-TiN/TiCN/α-Al2O3/TiN coated tools

Numerical Simulation of Surface Coating's Effect on Cutting Process

Tool failure mechanisms and cutting performance analysis during high-feed milling of 508-III steel

Molecular dynamics simulation of the diffusion behaviour between Co and Ti and its effect on the wear of WC/Co tools when titanium alloy is machined

Effect of MoS 2 element diffusion under high temperature condition on the tribological properties of cemented carbide materials

Analysis on the Wear Performances of Cemented Carbide Tools Containing Ti in the Coatings When Machining Ti-6Al-4V Alloys