Abstract:Thermal barrier coatings (TBCs) usually have complex structures and operate in cyclic high temperatures. The cracking phenomenon is usually observed at the interface with microscopic imperfections between the bond and the thermally grown oxide (TGO) layer owing to the cyclic plasticity around the defect interface under the cyclic thermal loading. Shakedown limits of TBCs with interface imperfections are investigated based on the proposed linear matching method considering the effect of temperature-dependent material properties. The influences of geometric parameters h(0), R/h(0) and H/R as well as the thermal expansion coefficient ratio alpha/alpha(r) are discussed in detail. Results present that the thickness of the TGO has no effect and the geometric factor R/h(0) shows a little influence on shakedown limits of the multilayered systems. However, the geometric parameter H/R and the thermal expansion coefficient ratio alpha/alpha(r) have a remarkable impact on shakedown limits. This indicates that the depth of the defect influences shakedown limits greatly, while the transition radius at the corner of the imperfection shows slight effect. This is obviously different from the common phenomenon that the transition radius usually has an important influence on shakedown limits. Based on the calculated data, the shakedown assessment approach of TBCs considering various factors mentioned above is proposed. It is of great interest that the simulated effective plastic strain occurs at the defect interface between the TGO and the bond layer when the applied load exceeds the shakedown limit. It is the crack failure region of cracked TBCs according to the microscopic morphology observation.

Investigation of Pile-Up Behavior for Thermal Barrier Coatings under Elevated-Temperature Indentation

An Elevated-Temperature Depth-Sensing Instrumented Indentation Apparatus for Investigating Thermo-Mechanical Behaviour of Thermal Barrier Coatings.

Use of Instrumented Micro-Indentation to Study the Mesoscopic Elasto-Plastic Behavior of Gh4145/Sq Superalloy During High-Temperature Cyclic Straining

High Temperature Fracture Toughness and Residual Stress in Thermal Barrier Coatings Evaluated by an In-Situ Indentation Method

Determination of high temperature mechanical properties of thermal barrier coatings by nanoindentation

Microstructure Parameters Affecting Interfacial Adhesion of Thermal Barrier Coatings by the EB-PVD Method

Determination of creep properties of thermal barrier coating (TBC) systems from the indentation creep testing with round flat indenters

Sintering Induced the Failure Behavior of Dense Vertically Crack and Lamellar Structured TBCs with Equivalent Thermal Insulation Performance

Sintering and Failure Behaviour of Eb-Pvd Thermal Barrier Coating after Isothermal Treatment

Residual Stresses in Thermal Barrier Coatings Measured by Photoluminescence Piezospectroscopy and Indentation Technique

Shakedown Analysis and Experimental Study of Thermal Barrier Coatings

Finite Element Simulation of Surface Micro-Indentation Behavior of Yttria Stabilized Zirconia Thermal Barrier Coatings with Microstructural Characteristic of Columnar Grains and Sub-Grains Based on a Nonlinear Contact Model

Numerical Analysis of the Influence of Pore Microstructure on Thermal Conductivity and Young's Modulus of Thermal Barrier Coating

High Temperature Hardness and Thermal Analysis of CoNiCrAlY Alloys Used As Bond Coats for Thermal Barrier Coatings

A Numerical Study of the Influence of Interface Morphology on the Stress Behavior in Thermal Barrier Coatings Near an Inclined Film-Cooling Hole

Thermal shock behaviors and failure mechanisms of EB-PVD thermal barrier coatings using radiant heating

Chemo-thermo-mechanical modeling of EB-PVD TBC failure subjected to isothermal and cyclic thermal exposures

Numerical and Experimental Studies on the In-Situ Measurement of Thermal Conductivity of the Thermal Barrier Coating

Experimental Study of High Temperature Failure Behavior of Thermal Barrier Coating Based on 3D Digital Image Correlation of Single camera

Shakedown Boundaries of Multilayered Thermal Barrier Systems Considering Interface Imperfections

Failure of Electron Beam Physical Vapor Deposited Thermal Barrier Coatings System under Cyclic Thermo-Mechanical Loading with a Thermal Gradient