Abstract:Failure of thermal barrier coating (TBC) systems is closely related to the temperature field and stress state of their components. The lack of accurate cross-scale analysis methods has made it difficult to clarify the mechanical properties and damage mechanisms of TBC interfaces. This study proposes a cross-scale modeling method for TBC called the thermal barrier coating master–slave model (TMSM). First, the TMSM is established based on Saint-Venant's principle, thermal elastoplastic mechanics theory, and the von Mises yield criterion, and its applicability is discussed considering mesh conditions, geometric conditions, and cyclic conditions. The advantages of the TMSM are then demonstrated by comparison with the slave model. Finally, the effects of material plasticity and oxide thickness on the damage of the TBC were analysed using the TMSM. The results showed that the boundary effect can be eliminated using the slave model with an interface side length of 160 μm. The interfacial axial stress obtained by the TMSM was greater than that obtained by the slave model. The thermal mismatch stress caused by thermal material expansion at high temperatures and the residual stress caused by material plasticity at the moment of cooling are the two main causes of TBC failure. When the thickness range of the oxide layer is 2–3 μm, the oxide layer will inhibit the maximum thermal stress during thermal cycles, which is supported by the results of fatigue experiments conducted under the same condition. This study provides a new approach for the cross-scale analysis of TBC and demonstrates the positive effect of thermally grown oxide thickness on the thermal shock resistance of TBC using numerical analysis.

Characterization of isothermal and cyclic thermal damage of EB-PVD TBCs with the help of the 3D-DIC technique

Chemo-thermo-mechanical modeling of EB-PVD TBC failure subjected to isothermal and cyclic thermal exposures

Thermal Shock Performance of CVD Tungsten Coating at Elevated Temperatures

Experimental and Numerical Simulations of ELM-like Transient Damage Behaviors to Different Grade Tungsten and Tungsten Alloys

A damage model to evaluate the mechanical properties in the medium-long life stage for coating system subjected to elevated thermal loads with 3D-DIC technique

THz-TDS characterization of stress evolution of EB-PVD TBCs under thermal cycling

Failure Characteristics and Life Prediction for Thermally Cycled Thermal Barrier Coatings

Failure of Electron Beam Physical Vapor Deposited Thermal Barrier Coatings System under Cyclic Thermo-Mechanical Loading with a Thermal Gradient

Experimental Study of High Temperature Failure Behavior of Thermal Barrier Coating Based on 3D Digital Image Correlation of Single camera

Failure Mechanism of EB-PVD Thermal Barrier Coatings under the Synergistic Effect of Thermal Shock and CMAS Corrosion

Failure behavior study of EB-PVD TBCs under CMAS Corrosion and Thermal Shock Cycles

Shakedown Analysis and Experimental Study of Thermal Barrier Coatings

A real time deformation evaluation method for surface and interface of thermal barrier coatings during 1100°C thermal shock

Fracture Behavior of TBCs with Cooling Hole Structure under Cyclic Thermal Loadings

Cross-scale modeling and elasto-plastic mechanical properties of TBC with 3D hill-like interface

Thermal shock behaviors and failure mechanisms of EB-PVD thermal barrier coatings using radiant heating

Simulation of Residual Stresses and Their Effects on Thermal Barrier Coating Systems Using Finite Element Method

Modeling 3D TGO dynamic growth and stresses and the resulting modes of buckling failure in thermal barrier coatings

Thermal Cycling Behavior of Thermal Barrier Coatings with MCrAlY Bond Coat Irradiated by High-Current Pulsed Electron Beam

Thermomechanical and Thermal Gradient Mechanical Fatigue Lifetime of Thermal Barrier Coating Systems

Performance and Failure Modes of Thermal Barrier Coatings Deposited by EB-PVD on Blades under Real Service Conditions in Gas Turbine