Abstract:Low-temperature co-fired ceramics (LTCC) technology plays an important role in passive integration and system-on-a-package (SOP). This Technology could co-fire active layers, substrates and electrodes together at a temperature under the fusion points of these prime components. The samples of Ba{[(Mg 0.8 Zn 0.2 ) 0.98 Y 0.02 ] 1/3 Ta 2/3 }O 3 (BMZYT) ceramics with 3 wt% La 2 O 3 -B 2 O 3 -ZnO(LBZ) glass-fluxed were synthesized by the conventional solid-state reaction. The effect of LBZ glasses on the sintering behavior, microstructure, phase composition and dielectric properties of BMZYT ceramics have been systematically studied. Different proportions of LBZ glass were added to BMZYT ceramics. With the LBZ addition has been increasing, there is no other phase generation. The sintering temperature of the glass-added BMZYT samples was lowered to 900°C compared with BMZYT which sintered at 1375°C. LBZ glass served as flux former and conduced to the reactive liquid-phase mechanism. A liquid phase generated by LBZ can greatly promote the densification. The BMZYT ceramics with 3 wt% LBZ sintered at 900°C for 6 h shows good microwave dielectric properties: ε r =22.29, Q×f=11051 GHz (f=6.923GHz), and τ f =5.69 ppm/°C.

Silver Co‐Firable Li2ZnTi3O8 Microwave Dielectric Ceramics with LZB Glass Additive and TiO2 Dopant

Silver Co-Firable Zntinb2o8 Microwave Dielectric Ceramics With Li2o-Zno-B2o3 Glass Additive

Microwave Dielectric Properties of the Low-Temperature-fired Li2ZnTi3O8–Li2TiO3 Ceramics for LTCC Applications

Microwave Dielectric Properties of TiO 2 -Added Li 2 ZnTi 3 O 8 Ceramics Doped with Li 2 O-Al 2 O 3 -B 2 O 3 Glass

Microwave Dielectric Properties and Low Temperature Firing of (1 − X)li2zn3ti4o12 –xli2tio3 (0.2 ≤ X ≤ 0.8) Ceramics with B2O3–CuO Addition

Effect of ZnO and B2O3 on the Sintering Temperature and Microwave Dielectric Properties of LiNb0.6Ti0.5O3 Ceramics

Low temperature sintering and dielectric properties of Li 2 ZnTi 3 O 8 –TiO 2 composite ceramics doped with CaO–B 2 O 3 –SiO 2 glass

Low-Temperature Firing and Microwave Dielectric Properties of Ca[(Li13Nb23)0.8Ti0.2]O3Ceramics with ZnB2O4Glass Addition

Novel Thermal-Stable Low Temperature Sintered Ba 2 LiMg 2 V 3 O 12 Microwave Dielectric Ceramics with ZnO-P 2 O 5 -Mno 2 Glass Addition

High-Q Microwave Dielectric Properties Of Li(Zn0.95co0.05)(1.5)Sio4 Ceramics For Ltcc Applications

Microwave Dielectric Properties of Ba 2 Ti 3 Nb 4 O 18 Ceramic Doped with ZnO–B 2 O 3 –sio 2 Glass and Its Compatibility with Silver Electrode

Low Temperature Sintering Of Low-Loss Zntio3 Microwave Dielectric Ceramics With Zn-B-Si Glass

Sintering Behavior and Microwave Dielectric Properties of LMZBS Glass Doped Li 3 Mg 4 NbO 8 Ceramics for LTCC Applications

Microwave dielectric properties and low temperature firing of (1 − )LiZnTiO LiTiO (0.2 ≤ ≤ 0.8) ceramics with BO–CuO addition

Microwave dielectric properties of low-temperature-fired MgNb2O6 ceramics for LTCC applications

The effect of composition on Li2(Mg0.3Zn 0.7)Ti3O8-xTiO2 microwave dielectric ceramics for low temperature co-fired ceramics technology application

Synthesis of Ba{[(Mg0.8Zn0.2)(0.98)Y-0.02](1/3)Tan(2/3)}O-3 Microwave Dielectric Ceramics with La2O3-B2O3-ZnO Glass for LTCC Application

Microwave Dielectric Properties and Low-Temperature Sintering of (zn0.8mg0.2)2sio4–tio2 Ceramics with Li2O–B2O3

Microwave dielectric properties of low-fired Li 2 ZnTi 3 O 8 –TiO 2 composite ceramics with Li 2 WO 4 addition

Microwave Dielectric Properties Of Low-Temperature-Fired Mgnb(2)O(6)Ceramics For Ltcc Applications

Low-Firing and Microwave Dielectric Properties of Ba2Ti9O20 with BaO–B2O3–ZnO Glass Addition