Synthesis of Macroscopic Single Crystals of Ge<sub>2</sub>Sb<sub>2</sub>Te<sub>5</sub> via Single-Shot Femtosecond Optical Excitation
Marc Zajac,Aditya Sood,Taeho R. Kim,Mianzhen Mo,Michael Kozina,Suji Park,Xiaozhe Shen,Burak Guzelturk,Ming-Fu Lin,Jie Yang,Stephen Weathersby,Xijie Wang,Aaron M. Lindenberg
DOI: https://doi.org/10.1021/acs.cgd.0c00816
IF: 4.01
2020-01-01
Crystal Growth & Design
Abstract:Using in situ electron diffraction techniques, we demonstrate that femtosecond optical excitation above a threshold fluence of the amorphous, as-deposited, phase change material Ge2Sb2Te5 creates large, 100 mu m scale single crystals. This is 2 orders of magnitude larger than previously reported grains synthesized via photoexcitation. Transmission electron microscopy shows that these large crystals are dewetted regions with a face-centered cubic structure. Energy-dispersive X-ray spectroscopy indicates that the crystals have the same composition as the initial amorphous phase. We present a theoretical model which shows that this arises from a crossover from a nucleation-dominated crystallization regime to a growth-dominated crystallization regime, and we show that the measured grain size is consistent with Johnson-Mehl-Avrami-Kolmogorov (JMAK) crystallization theory for temperatures near the melting temperature. The ability to grow macroscopic single crystals from an amorphous material, and on arbitrary amorphous substrates, opens up a large area of potential applications, as well as new opportunities for tuning the nucleation, growth, and switching characteristics of phase-change materials.