Abstract:Calcium silicate (CS) is a main component of Portland cement and is responsible for the strength development. Recent research has shown that dicalcium silicate cement (CSC) is bioactive and is a potential candidate for bone replacement. Traditionally, dicalcium silicate powder is synthesized by a solid state reaction or a sol-gel method. The solid-state reaction, however, usually needs a higher temperature and a longer calcination time. Furthermore, the dicalcium silicate powder made by the sol-gel method is not pure, and contains a significant quantity of CaO which is harmful to the strength and biological properties of the CSC. The Pechini technique is an alternative, low temperature polymeric precursor route for synthesis of high purity powders. In this study, purer CS powder was synthesized via the Pechini method by calcination at 800°C for 3h. DSC-TGA, XRD, SEM were used for characterization of CS powder and the hydrated cement. The DSC-TGA curves showed that the main exothermic peak was at 479°C and the total mass loss was 79.2%. The XRD patterns of CSC after hydration for 7, 14, and 35 days illustrated that dicalcium silicate hydrate (Ca1.5SiO3.5·xH2O, C-S-H) was formed in the hardened CS paste. The XRD peaks on the diffraction pattern of the C-S-H of the day 35 sample were of greater intensity than those at day 7 and day 14. This demonstrates that the hydration speed was slow and complete hydration could take more than one month. Flake-like crystals were observed on scanning electron micrographs following hardening. The degradation study result showed that there was no mass loss of CSC after the samples were soaked into phosphate buffered saline (PBS) for 40 days. The silicon assay revealed that orthosilicic acid could be released from CSC after the samples were soaked in simulated body fluid (SBF). Silicon is known to be critical to skeletal mineralization. The existence of silicon may stimulate the proliferation of bone and activate cells to produce bone. Investigation of cell attachment confirmed that the MC-3T3 cells attached well to the surfaces of CSC after seeding.

Mechanical Properties and Protein Adsorption of Ca-5(Po4)(2)Sio4 Bioceramics Sintered from Solid State Reaction Derived Powders

Effect of Α-Si3n4 on Mechanical Strength and Biological Activity of Silicocarnotite Bioceramic

Cytocompatibility and Osteogenic Activity of a Novel Calcium Phosphate Silicate Bioceramic: Silicocarnotite.

Performance Investigation of the Sol-Gel Porous Biomaterial of the System Cao-P2o5-Sio2 in Sbf Solution

Fabrication And Characterization Of Tricalcium Silicate Bioceramics With High Mechanical Properties By Spark Plasma Sintering

Preparation and Characterization of Casio3-Ca-3(Po4)(2) Composite Bioceramics

Surface Reactivity and Hydroxyapatite Formation on Ca5MgSi3O12 Ceramics in Simulated Body Fluid

Favorable Osteogenic Activity of Iron Doped in Silicocarnotite Bioceramic: in Vitro and in Vivo Studies.

Copper containing silicocarnotite bioceramic with improved mechanical strength and antibacterial activity

A Bioactive Ca2sib2o7 Ceramics and in Vitro Hydroxyapatite Mineralization Ability in Sbf

Porous Hydroxyapatite Bioceramics Prepared by Polymeric Sponge Impregnation Process

Controlling the Biological Activity and Mechanical Properties of Sol-Gel Synthesized Peg-Cao-Sio2-P2o5 Hybrid Materials for Bone Tissue Engineering

Fabrication and properties of CaSiO3/ Sr3(PO4)2 composite scaffold based on extrusion deposition

Synthesis of Pure Tricalcium Silicate Powder by the Pechini Method and Characterization of Hydrated Cement

Preparation and physical characterization of calcium sulfate cement/silica-based mesoporous material composites for controlled release of BMP-2

Preparation of Dense Β-Casio3 Ceramic with High Mechanical Strength and HAp Formation Ability in Simulated Body Fluid

Processing, Microstructures and Mechanical Properties of Aqueous Gelcasted and Solid-State-Sintered Porous Sic Ceramics

Bioactivity and Mechanical Properties of PDMS-modified CaO-SiO2-TiO2 Hybrids Prepared by Sol-Gel Process

Fabricating Of Polyphosphates Porous Bioceramics With Al2o3-Mgo-P2o5 Addition

Synthesis and Protein Adsorption of Calcium Silicate/Apatite Composite Powders

Fabricating of Polyphosphates Porous Bioceramics with Al 2 O 3 -Mgo-p 2 O 5 Addition