Abstract:With phenolic resin as carbon source, ethylene glycol as solvent and pore-forming agent, and silicon monoxide as pore-forming agent and silicon source, a kind of light hierarchical porous silicon carbide (SiC) ceramics with adjustable pores was prepared by gelcasting, carbonization and carbothermal reduction. With the addition of silicon monoxide in the green body from 13 to 49 % , the porosities increased from 66 to 89 % , the densities and thermal conductivity are as low as 0.36 g·cm ¹ 3 and 0.29 W·m ¹ 1 ·K ¹ 1 . The macropores are mainly determined by the addition of silica particle size, which increases from 9.2 to 39.5 % , while the micropores and mesopores, ranging from 56.8 to 49.5 % , are mainly determined by the pyrolysis of resin carbon source. When the porosity of porous SiC is 75 % , the compressive strength of 7.83 MPa can be reached. The prepared porous SiC ceramics possessed light, good thermal insulation and other properties, which can be further improved by changing the shape and size of the added SiO particles. In addition, di ﬀ erent from using polycarbosilane as preceramic polymer, the porous SiC ceramics with complex shape and uniform microstructure can be prepared via gelcasting, which will reduce the production costs and broaden its application.

Processing, Microstructures and Mechanical Properties of Aqueous Gelcasted and Solid-State-Sintered Porous Sic Ceramics

Fabrication, Structure and Properties of Porous SiC Ceramics with High Porosity and High Strength

Fabrication and Properties of SiC Porous Ceramics by Slip Casting Process

Gel casting and properties of porous silicon carbide/silicon nitride composite ceramics

Fabrication of Porous SiC Ceramics with Laminated Structure by Freeze Casting of Aqueous Slurries

Preparation And Properties Of Sic Ceramics Via Sls/Cip Process

Preparation of <i>In Situ</i> Synthesized SiC Particles Reinforced Highly Porous Si<sub>3</sub>N<sub>4</sub> Ceramics by Gel-Casting

Ultralight Porous SiC with Attracting Strength: Freeze Casting of Polycarbosilane/sicp/camphene-Based Suspensions

Influence of Fabricated Process on Mechanical Properties of Porous Sic-Particle/Si3n4 Composites

Microstructure and Property of Porous SiC Ceramics Prepared by Vacuum Sintering

Thermal Conductivity and Microstructure Properties of Porous SiC Ceramic Derived from Silicon Carbide Powder

Preparation And Properties Of High Strength Porous Si3n4 Ceramics

Effects of Sintering Additives on Microstructure and Properties of Porous SiC Ceramics with High Porosity

Microstructure and properties of porous Si3N4 ceramics by gelcasting-self-propagating high-temperature synthesis (SHS)

Fabrication and Characterization of Hierarchical Porous SiC Ceramics Via Gelcasting and Carbothermal Reduction Between Carbon and SiO

Microstructure and Mechanical Properties of Porous SiC Ceramics by Carbothermal Reduction and Subsequent Recrystallization Sintering

Preparation of in-situ synthesized SiC particles reinforced highly porous Si3N4 ceramics by gel-casting

Fabrication and Properties of SiC Porous Ceramics Using a Polyurethane Preparation Process

Preparation and Properties of Micro porous Si3N4 Ceramics by Gelcasting

Preparation of Porous Sio2 Ceramics by Gelcasting

Microstructure and Mechanical Properties of Silicon Carbide Woodceramics