Porosity of calcium metaphosphate glass ceramics as a kind of tissue engineering material
Yue-heng Wu,Shun-qing Tang,Xuan Mao,AH Cheng,WJ Tang,SL Du
DOI: https://doi.org/10.3321/j.issn:1673-8225.2007.01.035
2007-01-01
Abstract:A new kind of porous foaming glass ceramics was prepared by sintering twice without any foaming agent to investigate the porosity of glass ceramics, analyze the porosity mechanism, make a hypothesis of foaming and validate the degradation and biological compatibility. Without adopting any foaming agent, the porous foaming glass ceramics were prepared. The Ca/P (mol) ratio of the prescription in raw materials was 0.47, and the sintering temperature was 680 °C. There were mainly calcium metaphosphate (β-Ca (PO3)2, CMP) phases detected by X-ray diffraction. Liquid statics weighing method was adopted to calculate the water absorption (Wa), apparent porosity (Pa) and bulk density (Db) of CMP: 34.6%, 43.6% and 1.26 g/cm3 respectively, which were similar to the former study. Detection by scanning electron microscopy (SEM) showed that the holes of CMP glass ceramics were conterminous one another, and there were big (100-300 μm) and small (2-20 μm) size holes. The CMP had been dipped in the normal saline at 37 °C for 28 days, and the weight-losing rate was 9.2%, and the surface topography of the CMP materials was changed in some places, for example there were some unknown item mesh in CMP surface, which shall be probe into further. The cell experiments showed that human bone marrow stem cells combined tightly with the surface of CMP materials and were growing into the inner of the big size holes, which demonstrated that porous CMP glass ceramics could be prepared by sintering twice without any foaming agent, utilizing the prescription character of powerful degradation of CMP glass phase. The biocompatibility experiments disclosed that porous calcium metaphosphate CMP had good biological compatibility. It is proved to be an excellent tissue engineering material through the degradation and biocompatibility experiments.