Abstract:As a commonly used implant material, calcium sulfate cement (CSC), has some shortcomings, including low compressive strength, weak osteoinduction capability, and rapid degradation. In this study, silica-based mesoporous materials such as SBA-15 were synthesized and combined with CSC to prepare CSC/SBA-15 composites. The properties of SBA-15 were characterized by X-ray diffraction, transmission electron microscopy, and nitrogen adsorption-desorption isotherms. SBA-15 was blended into CSC at 0, 5, 10, and 20 wt%, referred to as CSC, CSC-5S (5% mass ratio), CSC-10S (10% mass ratio), and CSC-20S (20% mass ratio), respectively. Fourier-transform infrared spectroscopy and compression tests were used to determine the structure and mechanical properties of the composites, respectively. The formation of hydroxyapatite on composite surfaces was analyzed using scanning electron microscopy and X-ray diffraction after soaking in simulated body fluid. BMP-2 was loaded into the composites by vacuum freeze-drying, and its release characteristics were detected by Bradford protein assay. The in vitro degradation of the CSC/SBA-15 composite was investigated by measuring weight loss. The results showed that the orderly, nanostructured, mesoporous SBA-15 possessed regular pore size and structure. The compressive strength of CSC/SBA-15 increased with the increase in SBA-15 mass ratio, and CSC-20S demonstrated the maximum strength. Compared to CSC, hydroxyapatite that formed on the surfaces of CSC/SBA-15 was uniform and compact. The degradation rate of CSC/SBA-15 decreased with increasing mass ratio of SBA-15. The adsorption of BMP-2 increased and released at a relatively slow rate; the release rate of BMP-2 in CSC-20S was the slowest, and presented characteristics of low doses of release. In vitro experiments demonstrated that the physical properties of pure CSC incorporated with SBA-15 could be improved significantly, which made the CSC/SBA-15 composite more suitable for bone repair and bone-tissue engineering.

Synthesis and Protein Adsorption of Calcium Silicate/Apatite Composite Powders

Synthesis of mesoporous silica material with hydrophobic external surface and hydrophilic internal surface for protein adsorption

Characterization and Cytocompatibility of Premineralized Silk Fibroin/Chitosan Composite Scaffolds

Preparation And Characterization Of Plla/Casio3/Apatite Composite Films

Mechanical Properties and Protein Adsorption of Ca-5(Po4)(2)Sio4 Bioceramics Sintered from Solid State Reaction Derived Powders

Preparation and in vitro bioactivities of calcium silicate nanophase materials

Biomineralizing Synthesis of Mesoporous Hydroxyapatite–calcium Pyrophosphate Polycrystal Using Ovalbumin As Biosurfactant

Shield Effect of Silicate on Adsorption of Proteins Onto Silicon-Doped Hydroxyapatite (100) Surface.

Study of protein adsorption on octacalcium phosphate surfaces by molecular dynamics simulations

Calcined Hydroxyapatite Powders with Increased Chemical Stabilities and Dispersibility

Preparation and Characterization of Casio3-Ca-3(Po4)(2) Composite Bioceramics

Physico-chemical characteristics and protein adsorption potential of hydroxyapatite particles: influence on in vitro biocompatibility of ceramics after sintering

A Study of Adsorption Behaviour of Cu(II) on Hydroxyapatite-Coated-Limestone/Chitosan Composite

Preparation of Mesoporous Nano-Hydroxyapatite Using a Surfactant Template Method for Protein Delivery

The Preparation and Characterization of Chitosan/Calcium Phosphate Composite Microspheres for Biomedical Applications

Preparation and physical characterization of calcium sulfate cement/silica-based mesoporous material composites for controlled release of BMP-2

Calcium Phosphate/chitosan Composite Coating: Effect of Different Concentrations of Mg2+ in the M-Sbf on Its Bioactivity

Synthesis of Element-Substituted Hydroxyapatite with Controllable Morphology and Chemical Composition Using Calcium Silicate As Precursor

Calcium Silicate Nanopowder Preparaed by Chemical Precipitation Method and Its in vitro Bioactivities

Biomimetic Synthesis and Biocompatibility Evaluation of Carbonated Apatites Template-Mediated by Heparin.

Identification of Proteins Adsorbed on Hydroxyapatite Ceramics with a Preferred Orientation to a-Plane