Abstract:MnO2 nanorods with exposed (110), (100), or (310) facets were prepared and investigated for catalytic oxidation of chlorobenzene, then the (110)-exposed MnO2 nanorod was screened as the candidate parent and further modified by Pt and/or Mo with different contents. The loading of Pt enhanced activity and versatility of the pristine MnO2, but the polychlorinated byproducts and Cl2 were promoted, conversely, as the decoration of Mo inhibited the polychlorinated byproducts and improved durability. Determination of structure and properties suggested that Pt facilitated the formation of more oxygen vacancies/Mn3+ and surface adsorbed oxygen weakened the bonds of surface lattice oxygen, while Mo stabilized surface lattice oxygen and increased acid sites, especially Brønsted acid sites. Expectedly, Pt and Mo bifunctionally modified MnO2 presented a preferable activity, selectivity, and durability along with the super resistance to H2O, high-temperature, and HCl, and no prominent deactivation was observed within 30 h at 300 °C under dry and humid conditions, even at high-temperature aging at 600 °C and HCl-pretreatment (7 h). In this work, the optimized Mo and Pt codecorated MnO2 was considered a promising catalyst toward practical applications for catalytic oxidation of actual Cl-VOCs emissions.The Supporting Information is available free of charge at https://pubs.acs.org/doi/10.1021/acs.est.1c05086.The catalyst characterization information is provided together with the catalytic activity data, HRTEM, XRD, Raman, XPS, TG/DTG, UV–vis DRS, and DRIFTS spectra (PDF)This article has not yet been cited by other publications.

Low temperature chlorobenzene catalytic oxidation over MnOx/CNTs with the assistance of ozone

Catalytic Ozonation of Multiple Vocs at Low Temperature over a Potassium-Modified Mnox-Based Catalyst

Low-temperature Catalytic Oxidation of Chlorobenzene over MnOX/TiO2–CNTs Nano-Composites Prepared by Wet Synthesis Methods

Ozone Assisted Oxidation of Gaseous PCDD/Fs over CNTs-containing Composite Catalysts at Low Temperature.

Catalytic Oxidation of Chlorobenzene over Mnox/Al2o3-Carbon Nanotubes Composites

Enhanced catalytic oxidation of toluene over manganese-based multi-metal oxides synthesized by ozone driving redox reaction

Catalytic Oxidation of 1,2-Dichlorobenzene on V2O5–WO3/TiO2 Films: Effects of Ozone Addition and UV Irradiation

Ozone Promotion of Monochlorobenzene Catalytic Oxidation Over Carbon Nanotubes-Supported Copper Oxide at High Temperature

Adsorption and Catalytic Ozonation of Toluene on Mn/ZSM-5 at Low Temperature

Catalytic Degradation of 1,2-Chlorobenzene and Dioxins Coupled by Kinds of Methods

Comparative Investigation On Chlorobenzene Oxidation By Oxygen And Ozone Over A Mnox/Al(2)O(3 )Catalyst In The Presence Of So2

Catalytic Oxidation Of Chlorobenzene Over V2o5/Tio2-Cnts Nano Composites

Enhanced catalytic activities of MnOx/Co3O4 nanocomposites prepared via MOFs-templated approach for chlorobenzene oxidation

Unlocking efficient and robust ozone decomposition with CNT-confined manganese oxide via synergistic electronic modulation

Pt and Mo Co-Decorated MnO2 Nanorods with Superior Resistance to H2O, Sintering, and HCl for Catalytic Oxidation of Chlorobenzene.

Catalytic Oxidation of 1,2-Dcbz over V2O5/TiO2-CNTs: Effect of CNT Diameter and Surface Functional Groups.

Catalytic Ozonation of Toluene and Dichloromethane Mixture at Low Temperatures over Modified MnOx-based Catalyst

Catalytic Oxidation of Chlorobenzene over V2o5/Tio2-Carbon Nanotubes Composites

Pt and Mo Co-Decorated MnO 2 Nanorods with Superior Resistance to H 2 O, Sintering, and HCl for Catalytic Oxidation of Chlorobenzene

Metal-organic Frameworks Templated Micropore-Enriched Defective MnCeOx for Low Temperature Chlorobenzene Oxidation

Synergistic Effect for Simultaneously Catalytic Ozonation of Chlorobenzene and NO over MnCoOx Catalysts: Byproducts Formation under Practical Conditions