Abstract:In this study, transverse heat flow suppression (THFS) technique was proposed to enhance the ability of thermal-wave radar thermography (TWRT) to resist lateral thermal diffusion and uneven heating. The enhanced TWRT was used to detect subsurface defects of carbon fiber reinforced plastic (CFRP) laminates. The principle of THFS was described in detail by the optical flow analogy. The three-dimension (3-D) thermal-wave model stimulated by the uneven linear frequency modulation (LFM) thermal flow was introduced. The thermal-wave signal was processed by several different postprocessing characteristic extraction algorithms [Cross-correlation algorithm (CC), dual-orthogonal demodulation algorithm (DOD), fractional Fourier transform (FrFT), and principal component analysis (PCA)]. The comparison between normalized DOD amplitude/phase and normalized DOD-THFS amplitude/phase was carried out. The simulation results depicted THFS can significantly improve the difference between defect location and nondefect location. Nine CFRP specimens with artificial flat-bottom holes (FBHs) were prepared for nondestructive testing and evaluation (NDT&E) by enhanced TWRT. Seventy-two FBHs were prepared to test the probability of detection (PoD) of the enhanced TWRT. Hit/miss method was used to count defect information. The results demonstrated that the enhanced TWRT can realize the effective detection of defects (90% detection probability) with a diameter depth ratio of 5.06 under 95% confidence level. Compared with two state-of-the-art approaches, the proposed DOD-THFS phase has a better defect detection signal-to-noise ratio (SNR).

Inspection Of Defects In Cfrp-Foam Layered Structure Composite Plates Of Aerospace Materials Using Lock-In Thermography

Research on CFRP Materials Nondestructive Testing by IR Lock-in Thermography

Ultrasonic Inspection Of Localized Defects In Low-Porosity Cfrp

Non-destructive Testing of Airfoil Based on Infrared Lock-in Thermography

Inverse Heat Transfer Approach for Nondestructive Estimation the Size and Depth of Subsurface Defects of CFRP Composite Using Lock-in Thermography

Study on Lock-in Thermography Defect Detectability for Carbon-Fiber-Reinforced Polymer (CFRP) Sheet with Subsurface Defects

Defect Detection Method for CFRP Based on Line Laser Thermography

Theoretical and Experimental Study on Carbon/epoxy Facings-Aluminum Honeycomb Sandwich Structure Using Lock-in Thermography

Non-destructive Inspection of Carbon-Fibre-reinforced Polymers Using Lock-in Thermography

Intralaminar Crack Detection for Carbon Fiber Reinforced Polymers Based on Laser-Line Thermography

Ultrasonic Testing of Carbon Fiber-Reinforced Polymer Composites

Multi-frequency Fused Lock-in Thermography in Detecting Defects at Different Depths

A Study Of Detection Of Internal Defects In Cfrp Using Different Modes Of Planar Laser

Optimization of Thermal-Wave Radar Thermography by Transverse Heat Flow Suppression Technique for Accurate Defect Detection of CFRP Laminates

Detection and identification of delamination defects in CFRP laminates using nonlinear frequency-modulated infrared thermal wave testing technology

The fusion of lock-in phase images for the damage investigation in composites materials

Carbon fiber composites inspection and defect characterization using active infrared thermography: numerical simulations and experimental results

The Inspection of CFRP Laminate with Subsurface Defects by Laser Arrays Scanning Thermography (Lasst)

Debonding Defect Detection by Applying Pulsed, Lock-in and Linear Frequency Modulation Thermal Excitation Methods in the Inspection of Fiber-Reinforced Metal Laminates

Inspection of defects in composite structures using long pulse thermography and shearography

Defect detection and evaluation of ultrasonic infrared thermography for aerospace CFRP composites