HR-STEM investigation of atomic lattice defects in different types of η precipitates in creep-age forming Al–Zn–Mg–Cu aluminium alloy
Tsai-Fu Chung,Yo-Lun Yang,Cheng-Ling Tai,Makoto Shiojiri,Chien-Nan Hsiao,Cheng-Si Tsao,Wei-Chih Li,Zhusheng Shi,Jianguo Lin,Hsueh-Ren Chena,Jer-Ren Yang
DOI: https://doi.org/10.1016/j.msea.2021.141213
2021-05-01
Abstract:<p>High-resolution (HR) high-angle annular dark-field (HAADF) scanning transmission electron microscopy (STEM) has revealed the atomic lattice defects in different types of η precipitates in the Al-Zn-Mg-Cu aluminium alloy subjected to creep-age forming treatment (with a constant stress lower than its room-temperature yield strength during ageing). Along the zone axes of [110]<sub>Al</sub>//[2<span class="math"><math>1¯1¯</math></span>0]η of η<sub>1</sub> and η<sub>12</sub>, [112]<sub>Al</sub>//[2<span class="math"><math>1¯1¯</math></span>0]η of η<sub>2</sub> and [100]<sub>Al</sub>//[2<span class="math"><math>1¯1¯</math></span>0]η of η<sub>13</sub>, atomic projections of (2<span class="math"><math>1¯1¯</math></span>0)η have been investigated. In those types of η, elongated hexagonal lattice defects (labelled as Type I defects) can be found; they are apparently related to local disorder in atomic stackings. Furthermore, in η<sub>12</sub>, elongated hexagonal lattice defects with a much higher aspect ratio (labelled as Type II defects) are uniquely observed. These atomic lattice defects are presumably pertinent to the lattice accommodation in the course of creep-age forming. Additionally, in η<sub>1</sub> and η<sub>12</sub>, the features of a Penrose tiling defect connecting with Type I defects are observed, and these complex defects obviously affect the growth direction of the precipitate, resulting in a nearly spherical morphology. Alternatively, several entirely-passed faulted layers in a new type of precipitate, η<sub>14</sub>, consequently bring about a new orientation relationship: (51<span class="math"><math>3¯</math></span>)<sub>Al</sub>//(0001)η<sub>14</sub> and [112]<sub>Al</sub>//[2<span class="math"><math>1¯1¯</math></span>0]η<sub>14</sub>. Moreover, in an atomic STEM image of η<sub>14</sub>, the significant Z-contrast gradient adjacent to the transformation front of η<sub>14</sub> elucidates the Zn/Cu diffusion from the matrix to the precipitate along {1<span class="math"><math>1¯1¯</math></span>}<sub>Al</sub> planes at the interface.</p>
materials science, multidisciplinary,nanoscience & nanotechnology,metallurgy & metallurgical engineering