Abstract:Structural integrity assessment of reactor pressure vessels (RPVs) is essential for the safe operation of nuclear power plants. For RPVs in pressurized water reactors (PWRs), the assessment should be performed by considering neutron irradiation embrittlement and pressurized thermal shock (PTS) events. To assess the structural integrity of an RPV, a traditional method is usually employed by comparing fracture toughness of the RPV material with the stress intensity factor (KI) of a crack postulated near the RPV inner surface. When an underclad crack (i.e., a crack beneath the cladding of an RPV) is postulated, KI of this crack can be increased owing to the plasticity effect of cladding. This is because the yield stress of cladding is lower than that of base metal and the cladding may yield earlier than base metal. In this paper, detailed three-dimensional (3D) finite element analyses (FEAs) were performed in consideration of the plasticity effect of cladding for underclad cracks postulated in Japanese RPVs. Based on the 3D FEA results, a plasticity correction method was proposed on KI calculations of underclad cracks. In addition, the effects of RPV geometries and loading conditions were investigated using the proposed plasticity correction method. Moreover, the applicability of the proposed method to the case which considers the hardening effect of materials after neutron irradiation was also investigated. All of these results indicate that the proposed plasticity correction method can be used for KI calculations of underclad cracks and is applicable to structural integrity assessment of Japanese RPVs containing underclad cracks.

Effects of Plasticity on the Stress Intensity Factor Evaluation for Underclad Crack under Pressurized Thermal Shock Events

Investigation on the Plasticity Correction of Stress Intensity Factor Calculations for Underclad Cracks in Reactor Vessels

Plasticity Correction on Stress Intensity Factor Evaluation for Underclad Cracks in Reactor Pressure Vessels

Embedded Crack Treatments and Fracture Toughness Evaluation Methods in Probabilistic Fracture Mechanics Analysis Code for the PTS Analysis of RPV

Integrity Assessment Considering Unified Constraint for Reactor Pressure Vessel under Pressurized Thermal Shock

Importance of fracture criterion and crack tip material characterization in probabilistic fracture mechanics analysis of an RPV under a pressurized thermal shock

Re-Evaluation of the Structural Integrity of the Chinese Qinshan 300-MWe Reactor Pressure Vessel Under Pressurized Thermal Shock Using the Master Curve Method

Probabilistic Fracture Mechanics Analyses of Reactor Pressure Vessel under PTS Transients

Large Thermal Gradients on Structural Integrity of a Reactor Pressure Vessel Subjected to Pressurized Thermal Shocks

Fracture Studies on Cruciform Bend Specimens of Pressure Vessel Steel subjected to Thermo-mechanical Loading

Constraint characterization and fracture initiation analysis for semi-elliptical surface cracks in reactor pressure vessel

Theoretical Assessment of Burst Failure of Internally Pressurized Defect-Free Pipelines with Plastic Anisotropy

Loading Condition Evaluation for Structural Integrity Assessment of RPV Due to PTS Event Based on Three-Dimensional Thermal-Hydraulics and Structural Analyses

Effects of T-Stress on Fracture Behavior of Central-Cracked Stiffened Plate

Application of Flaw Updating Process on Probabilistic Integrity Analysis for a Reactor Pressure Vessel Subjected to Pressurized Thermal Shocks

Improvements to a probabilistic fracture mechanics code for evaluating the integrity of a RPV under transient loading

Sensitivity Analysis of Failure Probability on PTS Benchmark Problems of Pressure Vessel Using a Probabilistic Fracture Mechanics Analysis Code.

Effect of Coolant Water Temperature of Emergency Core Cooling System on Failure Probability of Reactor Pressure Vessel

Thermal-Mechanical performance analysis of a petal-shaped fuel rod under RIA condition

Study on Stress Intensity Factor of Girth Weld with Crack Defects

The Influence of Chemistry Concentration on the Fracture Risk of a Reactor Pressure Vessel Subjected to Pressurized Thermal Shocks