Abstract:A novel tungsten doping magnetic iron oxide catalyst was fabricated for selective catalytic reduction of NOx with NH3 (NH3-SCR), which was supported by carbon-included magnetic materials of Fe2O3-H synthesized by the solution combustion followed by the oxidization of hydrogen peroxide. As a consequence, the thermal stability of γ-Fe2O3 crystallites located in the magnetic support is significantly enhanced. Meanwhile, the irreversible transformation of Fe2O3 crystallites from γ-phase to α-phase during the annealing process at high temperatures (i.e. 400 °C) is restrained to a large extent. In addition, the magnetic W/Fe2O3 catalyst presents a superb porous structure with higher BET surface area and pore volume due to the anti-sintering effect of tungsten doping on the magnetic Fe2O3. In this regard, the surface acidity as well as the molar ratio of the surface-adsorbed oxygen is substantially augmented, leading to a remarkable improvement of the redox ability of the active bulk species in the catalyst. It is worth mentioning that the promotions in thermal stability and redox ability is affected by the doping amount of tungsten in the catalyst, the molar ratio of glucose/urea/iron, and the ignition temperature for synthesizing the magnetic iron oxide support. The experiments revealed that with a doping amount of 7.5 wt%, a molar ratio of glucose/urea/iron of 5:20:8, and an ignition temperature of 400 °C, the NH3-SCR activity of the novel catalyst could be optimized.

Selective catalytic reduction of NO with NH3 over novel iron–tungsten mixed oxide catalyst in a broad temperature range

Tailoring the Proceeding of the NH3-SCO and NH3-SCR Reactions over FeOx Catalysts by Modifying with NbOx

Selective Catalytic Reduction of NOx with NH3 over Short-Range Ordered W-O-Fe Structures with High Thermal Stability

Activity enhancement of WO3 modified FeTiO catalysts for the selective catalytic reduction of NO by NH3

Optimizing Selective Catalytic Reduction of NO with NH3 on Fe2O3/WO3 Via Redox‐Acid Synergy

Activity enhancement of WO<sub>3</sub> modified FeTiO<sub>x</sub> catalysts for the selective catalytic reduction of NO<sub>x</sub> by NH<sub>3</sub>

Activity Enhancement of Wo3 Modified Fe2o3 Catalyst for the Selective Catalytic Reduction of Nox by Nh3

Substitution of WO3in V2O5/WO3–TiO2by Fe2O3for Selective Catalytic Reduction of NO with NH3

Promotional effect of tungsten modification on magnetic iron oxide catalyst for selective catalytic reduction of NO with NH3

Fe-Mn/Al2O3 Catalysts for Low Temperature Selective Catalytic Reduction of NO with NH3

Selective Catalytic Reduction of NO by NH3 on Fe, Mn-based Catalysts

Low-Temperature Selective Catalytic Reduction of NOx with NH3 over Fe–Mn Mixed-Oxide Catalysts Containing Fe3Mn3O8 Phase

Insight into highly efficient FeOx catalysts for the selective catalytic reduction of NOx by NH3: Experimental and DFT study

Experimental and Density Functional Theory Studies on the Zeolite-Based Fe–Ni–W Trimetallic Catalyst for High-Temperature NOx Selective Catalytic Reduction: Identification of Active Sites Suppressing Ammonia Over-oxidation

Influence of WO on the performance of a CrO –WO catalyst for the selective catalytic reduction of NO with NH3

Highly efficient NH3-SCR of NO over MnFeW/Ti catalyst at low temperature: SO2 tolerance and reaction mechanism

Highly dispersed MnOx-FeO(x)supported by silicalite-1 for the selective catalytic reduction of NO(x)with NH(3)at low temperatures

Iron oxide-based catalysts for low-temperature selective catalytic reduction of NOx with NH3

Novel FeVO4 catalyst modified with NbTiOx for efficient selective catalytic reduction of NOx with NH3

Iron Oxide-Based Catalysts for Low-Temperature Selective Catalytic Reduction of NOxwith NH3

Investigating the Role of H4SiW12O40 in the Acidity, Oxidability and Activity of H4SiW12O40-Fe2O3 Catalysts for the Selective Catalytic Reduction of NO with NH3