Abstract:Lignite is widely used as the fuel for coal-fired power plants, and its flue gas temperature is about 50-100 degrees C higher than others. V2O5-WO3/TiO2 is extremely restricted in the selective catalytic reduction (SCR) of NO from the coal-fired power plants burning lignite due to the drop of NOx conversion, low N-2 selectivity, and volatility of vanadium pentoxide at high temperatures. Therefore, a more environmental-friendly SCR catalyst with excellent SCR activity and better N-2 selectivity at 350-450 degrees C should be developed for this application. In this work, sulfated Fe-Ti spinel catalyst was developed for the SCR of NO from the coal-fired power plants burning lignite. The drop of NOx conversion at high temperatures was mainly related to the simultaneous occurrence of the catalytic oxidization of NH3 to NO during the SCR reaction. Ti was incorporated into gamma-Fe2O3 to decease the oxidization ability of Fe3+ on the surface, and the sites for -NH2 adsorption and the active components for -NH2 oxidization were separated after the sulfation to decrease the probability of the collision between -NH2 adsorbed and Fe3+ on the surface. They both inhibited the catalytic oxidization of NH3 to NO over gamma-Fe2O3. However, the SCR reaction over gamma-Fe2O3 was simultaneously restrained after the incorporation Ti and the sulfation. Therefore, NOx conversion over gamma-Fe2O3 at high temperatures depended on the ratio of NH3 conversion through the catalytic oxidization of NH3 to NO to that through the SCR reaction. This ratio decreased after the incorporation of Ti, and it further decreased after the sulfation, resulting in an obvious promotion of NOx conversion at high temperatures. Therefore, sulfated Fe-Ti spinel showed excellent SCR activity, N-2 selectivity, and H2O+SO2 durability at 300-450 degrees C, which was suitable for the application in the coal-fired power plants burning lignite.

Substitution of WO3in V2O5/WO3–TiO2by Fe2O3for Selective Catalytic Reduction of NO with NH3

Tailoring the Proceeding of the NH3-SCO and NH3-SCR Reactions over FeOx Catalysts by Modifying with NbOx

Optimizing Selective Catalytic Reduction of NO with NH3 on Fe2O3/WO3 Via Redox‐Acid Synergy

In Situ DRIFTS Studies of NH3-SCR Mechanism over V2O5-CeO2/TiO2-ZrO2 Catalysts for Selective Catalytic Reduction of NOx

Selective Catalytic Reduction of NOx with NH3 over Short-Range Ordered W-O-Fe Structures with High Thermal Stability

Enhanced Catalytic Performance of V2O5–WO3/Fe2O3/TiO2microspheres for Selective Catalytic Reduction of NO by NH3

Activity Enhancement of Wo3 Modified Fe2o3 Catalyst for the Selective Catalytic Reduction of Nox by Nh3

Activity enhancement of WO3 modified FeTiO catalysts for the selective catalytic reduction of NO by NH3

Highly Efficient Mesoporous V2O5/WO3–TiO2 Catalyst for Selective Catalytic Reduction of NOx: Effect of the Valence of V on the Catalytic Performance

Novel FeVO4 catalyst modified with NbTiOx for efficient selective catalytic reduction of NOx with NH3

Improvement of the Activity of Γ-Fe2o3 for the Selective Catalytic Reduction of NO with NH3 at High Temperatures: NO Reduction Versus NH3 Oxidization

Fe-Ti spinel for the selective catalytic reduction of NO with NH 3: Mechanism and structure-activity relationship

SO2 Promoted V2O5-MoO3/TiO2 Catalyst for NH3-SCR of NOx at Low Temperatures

Selective catalytic reduction of NO with NH3 over novel iron–tungsten mixed oxide catalyst in a broad temperature range

Selective Catalytic Reduction of NO by NH3 on Fe, Mn-based Catalysts

VxMn(4-x)Mo3Ce3/Ti catalysts for selective catalytic reduction of NO by NH3

Effect of Synthesis Methods on Activity of V2O5/CeO2/WO3-TiO2 Catalyst for Selective Catalytic Reduction of NOx with NH3

Catalytic Performance, Characterization, and Mechanism Study of Fe-2(So4)(3)/Tio2 Catalyst for Selective Catalytic Reduction of Nox by Ammonia

Improved catalytic performance and resistance to SO2 over V2O5-WO3/TiO2 catalyst physically mixed with Fe2O3 for low-temperature NH3-SCR

Enhancement of Low-Temperature Activity of Γ-Fe2o3-Modified V2o5-Moo3/Tio2 Catalysts for Selective Catalytic Reduction of Nox with Nh3

Selective Catalytic Removal of High Concentrations of NOx at Low Temperature