Abstract:The selective catalytic reduction (SCR) of NOx with NH3 at high temperature (T > 500 degrees C) usually has low conversion efficiency due to the undesired NH3 over-oxidation. To suppress the oxidation of NH3 to NOx we proposed a Fe-exchanged zeolite catalyst with the modification of Ni and W for the NH3-SCR process, which was investigated in a wide temperature range (200-850 degrees C). It was found that the NH3 over-oxidation was significantly suppressed on the Fe-Ni-W trimetallic catalyst, leading to an improvement in the SCR performance. The catalyst characterizations suggest that the thermal tolerance of the acidity sites was enhanced and the active species in the multi-metal combined catalyst showed a higher valence state. To further identify the roles of active sites during NH3 oxidation, dehydrogenation, and transformation into intermediates, time-resolved in situ diffuse reflectance Fourier transform spectroscopy and density functional theory calculations were conducted. We found that the enhanced activity of catalysts at high temperature was ascribed to the Bronsted acid sites on the ZSM-5 lattice and extra-framework exchanged metal center that was affected by the topology confinement from zeolite. A high activation barrier for the rate-determining step of the NH3 oxidation process was observed on these active sites, thus inhibiting the oxidation side reaction. The findings provide rational strategies to modify mononuclear sites and synergetic restriction effect of multi-metal centers over zeolite-based catalysts for effective SCR at high temperatures.

Investigating the Role of H4SiW12O40 in the Acidity, Oxidability and Activity of H4SiW12O40-Fe2O3 Catalysts for the Selective Catalytic Reduction of NO with NH3

Tailoring the Proceeding of the NH3-SCO and NH3-SCR Reactions over FeOx Catalysts by Modifying with NbOx

Activity Enhancement of Wo3 Modified Fe2o3 Catalyst for the Selective Catalytic Reduction of Nox by Nh3

Activity enhancement of WO3 modified FeTiO catalysts for the selective catalytic reduction of NO by NH3

The Effect of SiO2 on a Novel CeO2–WO3/TiO2 Catalyst for the Selective Catalytic Reduction of NO with NH3

Fe2O3@SiTi Core-Shell Catalyst for the Selective Catalytic Reduction of NOx with NH3: Activity Improvement and HCl Tolerance

Selective Catalytic Reduction of NOx with NH3 over Short-Range Ordered W-O-Fe Structures with High Thermal Stability

Selective catalytic reduction of NO with NH3 over novel iron–tungsten mixed oxide catalyst in a broad temperature range

Structure, Acidity and Activity of CuOx/WOx–ZrO2 Catalyst for Selective Catalytic Reduction of NO by NH3

Optimizing Selective Catalytic Reduction of NO with NH3 on Fe2O3/WO3 Via Redox‐Acid Synergy

Effects of WO3 and SiO2 Doping on CeO2–TiO2 Catalysts for Selective Catalytic Reduction of NO with Ammonia

Improvement of sulfur and water resistance with Fe-modified S-MnCoCe/Ti/Si catalyst for low-temperature selective catalytic reduction of NO with NH3

Capability of molecular sieve-supported FeSO_4 catalyst for selective catalytic reduction of NO_x

Influence of WO on the performance of a CrO –WO catalyst for the selective catalytic reduction of NO with NH3

Insight into highly efficient FeOx catalysts for the selective catalytic reduction of NOx by NH3: Experimental and DFT study

Experimental and Density Functional Theory Studies on the Zeolite-Based Fe–Ni–W Trimetallic Catalyst for High-Temperature NOx Selective Catalytic Reduction: Identification of Active Sites Suppressing Ammonia Over-oxidation

Highly Dispersed MnOx–FeOx Supported by Silicalite-1 for the Selective Catalytic Reduction of NOx with NH3 at Low Temperatures

Understanding the high performance of an iron-antimony binary metal oxide catalyst in selective catalytic reduction of nitric oxide with ammonia and its tolerance of water/sulfur dioxide

Enhanced Catalytic Performance of V2O5–WO3/Fe2O3/TiO2microspheres for Selective Catalytic Reduction of NO by NH3

Investigation of the promotion effect of WO3 on the decomposition and reactivity of NH4HSO4 with NO on V2O5–WO3/TiO2 SCR catalysts

Activity enhancement of sulphated Fe<sub>2</sub>O<sub>3</sub> supported on TiO<sub>2</sub> -ZrO<sub>2</sub> for the selective catalytic reduction of NO by NH<sub>3</sub>