Abstract:The melting point of Ti:MgAl2O4 crystal is as high as 2130 °C, it is a challenge to obtain a large-sized and high-quality laser crystal. By optimizing the crystal growth process, Ti:MgAl2O4 crystal with a size of 30 mm× 70 mm is successfully grown by the Czochralski method under the condition of weak reducing atmosphere. The X-ray diffraction pattern is studied, and the x-ray rocking curve indicates that the grown crystal has a high crystalline quality in terms of the lower full width at half maximum(FWHM) intensity, which provides a material basis for the next laser output experiment. In a range of 100–1000 cm–1, there are four Raman vibration peaks located at 312, 410, 675 cm–1 and 771 cm–1 respectively. The grown crystal has an absorption cutoff range of 250–318 nm and two wide absorption bands of 395–495 nm and 550–1100 nm. Excited by 271 nm, the grown crystal shows a strong broadband emission ina range of 340–650 nm with a peak centered at 480 nm. After annealing in hydrogen atmosphere, shape of the transmittance spectrum and emission spectrum are both unchanged, but the fluorescent emission intensity is significantly reduced. After annealing in air atmosphere, the original two absorption bands disappear while none of the characteristics of fluorescence emission in a 340–650 nm range changes significantly. In addition, a new fluorescence emission peak near 725 nm is observed. Combining with the ESR spectrum, what we canconfirm is that the Ti:MgAl2O4 as-grown crystal contains Ti3+ and Ti4+ ions, and no ESR signal of Ti3+ is observed after annealing in air atmosphere. Moreover, excitationspectrum is also recorded. The fluorescence lifetime is 14 μs at room temperature, which is 4–5 times that of Ti:Al2O3 crystal and Ti:BeAl2O4 crystal. Furthermore, the emission cross section of the grown Ti:MgAl2O4 crystal is calculated from the Füchtbauer-Ladenburg (F-L) formula and its value is 2 × 10–20 cm2, large emission cross section which is beneficial for realizing laser oscillation. All the above results show that the Ti:MgAl2O4 crystal is a potential crystal material for realizing broadband tunable blue laser output.

Study on the Growth, Modification and Thermal Properties of Γ-Lialo2 Single Crystals

Study on the growth, modification and thermal properties of y-LIAIO2 single crystals

Influence of Vapor Transport Equilibration on the Crystal Quality and Thermal-Expansion Coefficients of Γ-Lialo2

RETRACTED: Phase Transition and Thermal Expansion of the LaAlO3 Single Crystal at High Temperatures

Study on the Growth Defects of Γ-Lialo2 Crystal

Study on Large-size γ-LiAlO2 Single Crystal Grown by Czochralski Technique

Structure and Residual Stress in Γ-Lialo2 Layer Fabricated by Vapor Transport Equilibration on (0 0 0 1) Sapphire

Crystal Growth, Characterization, and Properties of Nonlinear Optical Crystals of Li 0.5 Ag 0.5 GaTe 2 for Mid-Infrared Applications

Study on the Growth of Pure and Ga3+ Doped γ-LiAlO2 Crystals

Numerical Simulation of Β-Ga2o3 Single Crystal Growth by Czochralski Method with an Insulation Lid

Growth and Characterization of Ti:MgAl2O4 Laser Crystal by Czochralski Method

Growth, Structure and Thermal Properties of LuGdVO4 Mixed Crystal

Investigation of Langanite and Langatate Single Crystals for High Temperature Sensing

The Impact of Melt Transparency on Li2MoO4 Single Crystal Growth by the Czochralski Technique

Effect of High Temperature Thermal Treatment of (100) Γ-Lialo2 Substrate on Epitaxial Growth of ZnO Films by Plasma-Assisted Molecular Beam Epitaxy

Tuning the hardness and crack resistance through liquid–liquid phase separation in an aluminosilicate glass

Crystal growth and thermal properties of a LiY(MoO 4 ) 2 crystal

Crystallization of aluminosilicate glass with additive TiO2

Effect of Nucleation Temperatures and Time on Crystallization Behavior and Properties of Li2O–Al2O3–SiO2 Glasses

Growth and Properties of TSAG and TSLAG Magneto-Optical Crystals with Large Size

Crystal Growth, Spectroscopic Characterization, and Laser Operation of Tm/Mg: LiTaO_3 Crystal