Magneto-structural transformations and magnetocaloric effect in the Heusler type Ni48Cu2Mn36Sn14-xTix melt-spun ribbons
Yikun Zhang,Jianlong Ouyang,Xin Wang,Yun Tian,Zhongming Ren
DOI: https://doi.org/10.1016/j.matchemphys.2022.126527
IF: 4.778
2022-10-01
Materials Chemistry and Physics
Abstract:The Heusler type Ni–Mn-Z (Z = Ga, ln, Sn, or Sb) alloys with magneto-structural transformations (MSTs) have received widespread research interests due to the exhibition of multifunctional characters. To further understand MSTs and improve the magnetocaloric performance of these alloys, in this work, the Ti doped Ni48Cu2Mn36Sn14-xTix (x = 0, 1, 2, 3) ribbons have been fabricated and systematically determined with regard to the structural, magnetic, and magnetocaloric properties by means of X-ray diffraction (XRD), scanning electron microscope (SEM), differential scanning calorimetry (DSC), and magnetization measurements. All the ribbons are found to crystallize in the ordered cubic L21 austenite phases at room temperature and with the equiaxed austenite morphology. With the increasing Ti content, the average grain size and the MST temperature increase but the austenite Curie temperature (T A C) decrease gradually. Moreover, the thermal hysteresis and magnetic hysteresis loss are greatly reduced with the Ti doping. The value of average hysteresis loss (AHL) is reduced from 86 Jkg−1 for Ti0 to 25.5 Jkg−1 for Ti3 ribbon under 7 T. Additionally, enhanced magnetocaloric effect has been observed by Ti-doping. With the magnetic field change (ΔH) of 0–7 T, the largest value of magnetic entropy change reaches 15.4 Jkg−1K−1 (Ti2) among the Ni48Cu2Mn36Sn14-xTix ribbons. The present work indicates that reasonable Ti doping could be a useful way to regulation the MSTs and improve the magnetocaloric performance of the Heusler type Ni–Mn–Sn-based alloys.
materials science, multidisciplinary