Phase formation and magnetic properties of annealed mechanical alloying Nd-Fe-V-Ti alloys and their nitrides

S.L Tang,C.H Wu,X.M Jin,B.W Wang,G.S Li,B.Z Ding,Y.C Chuang
DOI: https://doi.org/10.1016/S0925-8388(97)00250-8
IF: 6.2
1998-01-01
Journal of Alloys and Compounds
Abstract:Phase formation in annealed mechanical alloyed NdFe10.5+xV1.5(1−x)Tix, and magnetic properties of the consequent phases and their nitrides were investigated by using X-ray diffraction and magnetic measurement. From the X-ray diffraction patterns we have constructed a phase formation diagram as a function of Ti content x and annealing temperature. The demarcation curve between 1:7 and 1:12 phases moves to higher annealing temperatures with increasing Ti content. In the NdFe11Ti alloy the ThMn12 structure is obtained by annealing the as-milled powder at temperatures above 950°C. The nitrides NdFe10.5+0.5xV1.5(1−x)TixNy retain the same structure as their parent compounds. The nitride with high V content is more stable than that with low V content. Upon nitrogenation, the Curie temperature is enhanced from 150°C to 180°C. In NdFe10.5+0.5xV1.5(1−x)TixNy Tc the values fall in the range 450∼480°C. The hard magnetic properties of NdFe10.5+0.5xV1.5(1−x)TixNy magnets have been assessed.
What problem does this paper attempt to address?