Phase Transformation and Magnetic Properties of Mechanically Alloyed Ndfe12-Xmoxny

SL Tang,XM Jin,BW Wang,ZQ Jin,SY Zhang,YW Du

DOI: https://doi.org/10.1016/s0925-8388(98)00667-7

IF: 6.2

1998-01-01

Journal of Alloys and Compounds

Abstract:The structure and permanent magnetic properties of isotropic powders of NdFe12−xMox (1≤x≤2) and their nitrides were investigated by using mechanical alloying. It was found that heat treatment of as-milled powders at 850∼900°C resulted in the formation of the Nd(Fe,Mo)12 phase. The metastable Nd(Fe,Mo)7 phase and a large amount of α-Fe were present at 800°C. After nitrogenation, the volume expansion of NdFe12−xMox phases was about 3.5% and the Curie temperature of the samples was enhanced by 157∼207°C. In NdFe12−xMoxNy compounds the values of Tc fall in the range of 272∼375°C. It has been found that the intrinsic coercivities strongly increased with increasing Mo content. The maximum coercivity, iHc=7.8 kOe, was achieved at 850°C for the sample with x=2. The difference between the coercivities of the mechanically alloyed Nd(Fe,Mo)12Ny powders with different Mo content was attributed to their different crystallization behavior.