Effect of melt-spinning speed on the microstructure and magnetic properties of Al–Cu–Fe alloy-doped SmCo5 ribbons
Li-Zhu Wang,Shu Wang,Zhi-Ying Zhang,Hong-Wei Wang,Ji-Bing Sun,Chun-Xiang Cui
DOI: https://doi.org/10.1007/s00339-021-04359-2
2021-02-25
Applied Physics A
Abstract:Multielement alloy doping is the feature of this paper, and disclosing the relationship between non-equilibrium microstructure and magnetic properties after rapid cooling is the key point. 3 wt% eutectic Al<sub>82.8</sub>Cu<sub>17</sub>Fe<sub>0.2</sub> alloy was doped into SmCo<sub>5</sub> alloy, followed by melt-spinning at 10–40 m/s. It is found all ribbons are composed of Sm(Co, M)<sub>5</sub> and Sm<sub>2</sub>(Co, M)<sub>7</sub> phases, but non-equilibrium solidification at different cooling rates results in different distribution characteristics of phases and magnetic properties of the ribbons. The 10 m/s ribbons are composed of Sm–Cu- and Co-rich Sm(Co, M)<sub>5</sub> phases and then the lamellate Sm<sub>2</sub>(Co, M)<sub>7</sub> coexists with CeCo<sub>5</sub>-type Sm(Co, M)<sub>5</sub> grains in the 25 m/s ribbons, while the 40 m/s ribbons form a cellular microstructure with Sm<sub>2</sub>(Co, M)<sub>7</sub> grain boundaries and Sm(Co, M)<sub>5</sub> intracellular grains. Correspondingly, the coercivity, remanence, and maximum magnetization of 40 m/s ribbons are 74.3%, 64.3%, and 53.2% higher than those of 10 m/s ribbons. At the same time, the coercivity mechanism and microstructure evolution are discussed.