Abstract:The effects of Co substitution for Fe on the spin reorientation temperature, magnetic properties over a wide temperature range, the thermal stability and on exchange enhancement in nanocrystalline (Nd/Pr)z(Fe1−xCox)94−zB6 alloys have been comprehensively studied. Such Co substitution substantially increased the Curie temperature (TC) of the 2/14/1 phase and slightly decreased the spin reorientation temperature (TSR) for these alloys. Despite the smaller anisotropy field for the Nd2Co14B phase, in comparison with Nd2Fe14B, a small Co substitution did not greatly decrease the room temperature (RT) coercivity jHC, regardless of the rare earth to transition metal ratio. The remanence Jr at RT was generally slightly improved by Co substitutions up to ~20%, though less so for the 8 at% rare earth (RE) series having a high volume fraction of soft magnetic phase. Similarly, substitution of up to 20% Co slightly enhanced the maximum energy product (BH)max at RT, except for the 8 at% RE alloys which showed a marked decline beyond 10 at% Co due to the strongly diminished jHC. In the case of the sub-ambient magnetic properties, Co substitution markedly decreased Jr and (BH)max, though the effect on jHC was much smaller. In contrast, Co additions, because of the enhancement of Tc, substantially improved the elevated temperature behaviour of all experimental alloys, by decreasing the values of the temperature coefficients for Jr and iHc, α and β, respectively, particularly for α. Moreover, the Co also reduced the irreversible losses in Jr and jHC measured on ribbon samples. Analysis of microstructural parameters governing the coercivity, using the modified Brown equation, suggested that Co substitution not only reduced the stray fields, by homogenizing the grain structure and smoothing the grain boundaries, but also improved the exchange coupling between grains.

Beneficial Effect of the Substitution of Co for Fe on the Magnetic Properties of Melt-Spun Pr2Fe14C/α-Fe-type Nanocomposite Magnets

Effect of Co Addition on the Phase Structure and Magnetic Properties of Fe-Si-Al Alloys

Novel Exchange-Coupled SmFe3/α-Fe Nanocomposite Magnets Fabricated by Magnetic Annealing

Magnetic reversal and magnetic memory effect in melt-spun Pr2Fe14B/α-Fe nanocomposite ribbons

Magnetic Properties of Pr–Fe–B Melt-Spun Ribbons with High Coerecivity

Influence of Co substitution for Fe on the magnetic properties of nanocrystalline (Nd,Pr)-Fe-B based alloys

The Microstructure and Magnetization Behaviors of (pr8.2fe86.1−xcoxb5.7)0.99zr0.01 (x = 0–10) Nanocomposite Magnets

Structure and Magnetic Properties of Pr2fe14(C,B)-Type Ribbons with High Coercivity

High-Performance Pr2fe(14)C-Type Magnets Prepared by Melt Spinning

Enhancement of magnetic properties of nanocomposite Pr2Fe14B/α-Fe magnets by small substitution of Dy for Pr

Effects of Nd and Co on thermal stability of nanocomposite Nd2Fe14B/a-Fe magnets

High coercivity Pr2Fe14B/α-Fe nanocomposite permanent magnets with Zr addition

Effects of Co Substitution for Fe on the Magnetization Process of Nanocrystalline Fe–Nb–B Alloys

Microstructure refinement and significant improvements of magnetic properties in Pr2Fe14B/α-Fe nanocomposites

Coercivity Enhancement in Pr9.5Fe83Zr2B5.5 Magnetic Nanomaterials

Coercivity mechanism and magnetization reversal process in nanocomposite Pr2Fe14B/α‐Fe alloy with Phosphorous addition

Towards the difference in coercivity enhancement of nanocrystalline Nd-Fe-B alloys with Pr and Ho substitution

Effects of Nb and Zr additions on crystallization behavior, microstructure and magnetic properties of melt-spun (Nd,Pr)2Fe14B/α-Fe alloys

Effect of P and Zr on the microstructure and magnetic properties of nanocomposite Pr2Fe14B/α-Fe ribbons

Hard magnetic properties and microstructures of melt-spun SmCo5Fex (x = 0, 1 and 2) ribbons

Hard magnetic properties and microstructures of melt-spun SmCo<sub>5</sub>Fe<sub><i>x</i></sub>(<i>x</i>= 0, 1 and 2) ribbons