Phase Formation and Magnetic Properties of (Y1−xSmx)Co5 Melt-Spun Ribbons

Xiang Liu,Siyue Yang,Xingping Zheng,Feilong Dai,Qingrong Yao,Jiang Wang
DOI: https://doi.org/10.3390/met14050562
IF: 2.695
2024-05-11
Metals
Abstract:Using X-ray diffraction (XRD) and a vibrating sample magnetometer (VSM), the effects of Sm substitution, wheel speed, and annealing temperature on the phase formation and magnetic properties of (Y1−xSmx)Co5 (x = 0.2, 0.3, 0.4, 0.5) melt-spun ribbons were investigated. The results indicate the following: (1) With the increase in Sm substitution, it was found that (Y1−xSmx)Co5 ribbons are entirely composed of the (Y-Sm)Co5 phase with a CaCu5-type structure. Additionally, the coercivity gradually increases, while the remanence and saturation magnetization gradually decrease. (2) As the wheel speed increases, the (Y1−xSmx)Co5 ribbons exhibit an increasing proportion of (Y-Sm)Co5 phase until reaching a speed of 40 m/s, where they are entirely composed of the (Y-Sm)Co5 phase. Magnetic measurements show that the coercivity (Hcj) and remanence (Br) of (Y0.5Sm0.5)Co5 ribbons increase gradually with increasing wheel speed, while saturation magnetization decreases. The variation in magnetic properties is mainly attributed to the formation of nucleation centers for reversed magnetic domain (2:7 and 2:17 phases); (3) (Y0.5Sm0.5)Co5 ribbons are composed of the (Y-Sm)Co5 phase and a small amount of the Sm2Co7 phase after annealing at 550 °C, 600 °C, and 650 °C. Temperature elevation promotes crystallization of the amorphous phase, resulting in a gradual decrease in coercivity, while the remanence and saturation magnetization exhibit an overall increasing trend. Through continuous optimization of the process, favorable magnetic properties were achieved under the conditions of a 0.5 Sm substitution level, a wheel speed of 40 m/s, and an annealing temperature of 550 °C, with a coercivity of 7.98 kOe, remanence of 444 kA/m, and saturation magnetization of 508 kA/m.
materials science, multidisciplinary,metallurgy & metallurgical engineering
What problem does this paper attempt to address?
The problems that this paper attempts to solve mainly focus on the following aspects: 1. **Influencing factors of phase structure and magnetic properties**: - **Effect of samarium (Sm) substitution**: Study the influence of different proportions of samarium substituting yttrium (Y) on the phase structure and magnetic properties of (Y\(_{1 - x}\)Sm\(_x\))Co\(_5\) melt - spun ribbon materials. - **Effect of wheel speed**: Explore the changes in the phase structure and magnetic properties of (Y\(_{1 - x}\)Sm\(_x\))Co\(_5\) melt - spun ribbon materials at different wheel speeds. - **Effect of annealing temperature**: Analyze the influence of different annealing temperatures on the phase structure and magnetic properties of (Y\(_{1 - x}\)Sm\(_x\))Co\(_5\) melt - spun ribbon materials. 2. **Optimizing magnetic properties**: - By systematically studying the above factors, look for the best preparation conditions to obtain (Y\(_{1 - x}\)Sm\(_x\))Co\(_5\) melt - spun ribbon materials with excellent magnetic properties. The specific goal is to achieve high coercivity, remanence and saturation magnetization under specific samarium substitution levels, wheel speeds and annealing temperature conditions. ### Specific problem description - **Effect of samarium substitution**: - As the amount of samarium substitution increases, the (Y\(_{1 - x}\)Sm\(_x\))Co\(_5\) ribbon is completely composed of the (Y - Sm)Co\(_5\) phase, and the coercivity gradually increases, while the remanence and saturation magnetization gradually decrease. - These changes are mainly attributed to the formation of reverse magnetic domain nuclei (2:7 and 2:17 phases). - **Effect of wheel speed**: - As the wheel speed increases, the proportion of the (Y - Sm)Co\(_5\) phase in the (Y\(_{1 - x}\)Sm\(_x\))Co\(_5\) ribbon gradually increases until the ribbon is completely composed of the (Y - Sm)Co\(_5\) phase when the wheel speed reaches 40 m/s. - Magnetic measurement results show that the coercivity and remanence of the (Y\(_{0.5}\)Sm\(_{0.5}\))Co\(_5\) ribbon gradually increase as the wheel speed increases, while the saturation magnetization gradually decreases. - **Effect of annealing temperature**: - After annealing at 550°C, 600°C and 650°C, the (Y\(_{0.5}\)Sm\(_{0.5}\))Co\(_5\) ribbon is mainly composed of the (Y - Sm)Co\(_5\) phase and a small amount of Sm\(_2\)Co\(_7\) phase. - The increase in temperature promotes the crystallization of the amorphous phase, resulting in a gradual decrease in coercivity, while the remanence and saturation magnetization generally show an increasing trend. ### Conclusion Through continuous optimization of the preparation process, under the conditions of a samarium substitution level of 0.5, a wheel speed of 40 m/s and an annealing temperature of 550°C, a (Y\(_{0.5}\)Sm\(_{0.5}\))Co\(_5\) ribbon with a coercivity of 7.98 kOe, a remanence of 444 kA/m and a saturation magnetization of 508 kA/m was obtained, achieving good magnetic properties.