Permanent magnetic properties of melt-spun Sm2(Fe, M)15Ga2C (M = Cu, Nb, Zr, Ti, V, Mo) ribbons

,Hongwei Zhang,Baogen Shen,Tsungshune Chin

DOI: https://doi.org/10.1088/0022-3727/31/23/006

1998-01-01

Abstract:The crystal structure and magnetic properties of Sm-2(Fe, M)(15)Ga2C ribbons prepared by melt-spinning and subsequent heat treatment were studied, where M represents Cu, Nb, Zr, Ti, V and Mo. The as-spun ribbons have an almost amorphous structure, and the annealed ribbons consist of 2:17 carbides and a small amount of alpha-Fe phase. Additions of Nb, Zr, Ti, V and Mo prevent crystalline grain growth. A significant coercivity enhancement was found only in Sm2Fe15-xCuxGa2C ribbons with x less than or equal to 1, and the maximum coercivity mu(0)H(ci) = 2.2 T at room temperature was obtained for melt-spun ribbons with x = 1 annealed in vacuum. The coercivity can be further improved for ribbons of higher carbon content annealed in a Sm atmosphere. Additions of M = Nb, V and Mo do not obviously change the coercivities in Sm2Fe14MGa2C ribbons annealed below 1173 K, but the coercivities for M = Zr and Ti ribbons decrease greatly. A small Cu addition (x less than or equal to 1) has little effect on the lattice parameters and Curie temperature, but decreases the saturation magnetization and the magnetocrystalline anisotropy field. Additions of Nb, Zr, Ti, V and Mo decrease the Curie temperature, the magnetocrystalline anisotropy field and the saturation magnetization.