The Magnetic Properties of Melt-Spun Nd9Fe85−xMnxB6(x=0–1) Ribbons

GZ Xie,ZJ Tian,Z Yu,BX Gu,M Lu,YW Du
DOI: https://doi.org/10.1016/s0304-8853(02)00485-7
IF: 2.707
2002-01-01
Physics Letters A
Abstract:The magnetic properties of Nd9Fe85−xMnxB6 (X=0,0.5,1) exchange coupling magnets were investigated by differential thermal analysis, X-ray diffraction, vibrating sample magnetometer and Mössbauer spectroscopy. It was found that manganese addition in melt-spun Nd9Fe85B6 can promote crystallization and enhance both coercivity and remanence ratio. The optimum coercivity and remanence ratio increases from 4.3kOe and 0.70 to 5.0kOe and 0.72, respectively. Thermomagnetic analysis showed Mn doping reduces the Curie temperature of the Nd2Fe14B phase and raises that of α-Fe phase. The volume fractions of α-Fe and Nd2Fe14B phase measured by Mössbauer spectroscopy appeared slightly different from Mn addition content. It is presumed that the enhancements in hard magnetic properties may be attributed to the change of the environment for the phases due to Mn addition.
What problem does this paper attempt to address?