Magnetic Properties of Mn Substituted Nd–Fe–B Composite

Guangyuan Xie,Jianhong Xu,Pinghua Lin,Gu B,M. Lu,Youwei Du,Yuan Zhou

DOI: https://doi.org/10.1016/j.jmmm.2003.11.379

IF: 3.097

2004-01-01

Journal of Magnetism and Magnetic Materials

Abstract:A study on the magnetic properties of Nd 9 Fe 85− x Mn x B 6 ( x =0–2) melt-spun ribbons has been investigated. Under optimal heating condition, it was found that an appropriate amount of Mn could enhance hard magnetic properties, especially the maximum coercivity, which increases more than about 20%. Higher amounts of Mn addition lead to a loss of coercivity and ( BH ) max . XRD results indicate that each alloy consists of hard magnetic Nd 2 Fe 14 B phase and soft magnetic α-Fe phase. TMA scans indicate that the Curie temperature ( T c ) of α-Fe phase rises with the Mn doping content increasing until x =2. For x =2 sample there is a slope between the Nd 2 Fe 14 B phase and α-Fe phase peaks in TMA curve. It can be attributed to the formation of the metastable Nd 2 Fe 23 B 3 phase. The change in magnetic properties and Curie temperature may be attributed to the formation of δ -Mn and R 2 Fe 23 B 3 phase.