Effect of Fe doping on the magnetic properties of MnBi alloy
Yang Yang,Jung Tae Lim,Hui-Dong Qian,Jihoon Park,Jong-Woo Kim,Oi Lun Li,Chul-Jin Choi
DOI: https://doi.org/10.1016/j.jallcom.2020.157312
IF: 6.2
2021-02-01
Journal of Alloys and Compounds
Abstract:<p>Structure and magnetic properties of Fe-doped MnBi alloy with a range of Fe concentrations were systematically investigated. The coercive field and saturation magnetization (<em>M</em><sub>s</sub>) were drastically changed according to the fabrication methods and Fe contents. The addition of Fe element could enhance the coercivity (<em>H</em><sub>c</sub>) of the MnBi-based alloy, and the increased <em>H</em><sub>c</sub> of 1.76 T was reached in the Mn<sub>55</sub>Bi<sub>45</sub>-Fe (15 <em>wt</em>%) ball-milled ribbon. Moreover, a high remanence ratio (<em>M</em><sub>r</sub>/<em>M</em><sub>s</sub>) of 97.0% was achieved in the Mn<sub>55</sub>Bi<sub>45</sub>-Fe (7.5 <em>wt</em>%) ball-milled ingot. In addition, as the concentration of Fe increases from 0 to 15 <em>wt</em>%, the Curie temperature (<em>T</em><sub>c</sub>) was increased from 635 to 652 K. This demonstrates that Fe-doped MnBi rare-earth permanent magnets could be a promising candidate for high-temperature applications. The relationship between magnetic properties and intermetallic lattice variations were discussed with precise Rietveld refinement analysis.</p>
materials science, multidisciplinary,chemistry, physical,metallurgy & metallurgical engineering