Effect of Cu and Cu–Ti additions on the microstructures and magnetic properties of Nd2Fe14B–α-Fe nanocomposite magnets

Sen Yang,Xiansong Liu,Shandong Li,Wen Qin,Xiaoping Song,Mu Lu,Youwei Du

DOI: https://doi.org/10.1016/S0925-8388(03)00128-2

IF: 6.2

2003-01-01

Journal of Alloys and Compounds

Abstract:The effect of Cu and Cu–Ti additions on the microstructures and magnetic properties of Nd2Fe14B–α-Fe nanocomposite magnets prepared by melt spinning have been investigated. The results show that Cu can form clusters serving as heterogeneous nucleation sites for α-Fe phase to enhance its nucleation kinetics. But in the ribbons with a combined Cu and Ti additions, the crystallization temperature is increased and a metastable hexagonal phase with TbCu7-type structure is formed prior to the α-Fe and Nd2Fe14B phase. With increasing the annealing temperature, the metastable 1:7 phase is decomposed into the α-Fe and Nd2Fe14B phases, which is propitious to form the more uniform microstructure with fine, soft α-Fe grains. When the contents of Cu and Ti reach 1.0 and 0.5 at.% respectively, the optimal magnetic properties iHc=4.8 kOe, σr=110 emu/g, (BH)max=15 MGOe were obtained after annealing at a temperature of 650°C for 8 min.