Effect of Nd-Co on microstructure and magnetic properties of Nd-Ce-Y-Fe-B sintered magnets
Zhi Jia,Mingpeng Kou,Shuai Cao,Xintong Yang,Guangfei Ding,Shuai Guo,Xiaodong Fan,Bo Zheng,Renjie Chen,Aru Yan
DOI: https://doi.org/10.1016/j.rinp.2022.105829
IF: 4.565
2022-08-01
Results in Physics
Abstract:The magnetic properties and microstructure of Nd-Ce-Y-Fe-B magnets with Nd-Co boundary additions (0, 1, 3, and 5 wt%) have been systematically investigated. The coercivity, remanence, and Curie temperature of the magnets showed to be all simultaneously improved with appropriate Nd-Co addition, especially, a significant coercivity increase of 15% accompanied with the remanence optimization was obtained at 3 wt% Nd-Co addition. The analyses revealed that the coercivity enhancement was attributed to the widened grain boundary width and the reduced magnetic exchange coupling between grains by the Nd-Co intergranular introduction. By designing the partial substitution, e.g. Co for Fe and Nd for Ce in matrix phase grains, the remanence improvement was achieved with the increased net magnetic moment, compensating the magnetic dilution brought by the extra alloy additions. Meanwhile, the Curie temperature of the magnet was improved with the weakened negative interaction. The combined intrinsic and microstructural modification in this study provides new insights into the preparation of high-abundance magnets with high coercivity, high remanence, and excellent temperature stability.
physics, multidisciplinary,materials science