Thermal Behaviour and Magnetic Properties of B-Rich Ndfeb Nanocomposite Hard Magnetic Alloys with Partial Substitution of Dy for Nd

SD Li,BX Gu,S Yang,H Bi,YD Dai,ZJ Tian,GZ Xie,YW Du,ZR Yuan

DOI: https://doi.org/10.1088/0022-3727/35/8/302

2002-01-01

Abstract:B-rich NdFeB base alloys with partial substitutions of Dy for Nd ((Nd1-xDyx)(4.5)Fe77B18.5 (x = 0-0.4)) were chosen to study the influence of Dy on thermal behaviour and magnetic properties. It was found that partial substitution of Dy for Nd results in a dramatic enhancement of coercivity H-j(c) from 183 to 261 kA m(-1) and of maximum magnetic product (BH)(max) from 1 10.6 to 133.7 kJ m(-3). However, the saturation magnetization M-s only decreases about 22.8 kA m(-1) for every 0.1 increment of Dy content x. Differential thermal analysis traces show that the crystallization process of the initial amorphous ribbons is a three-peak process. X-ray diffraction and differential thermal analysis indicate that the three peaks correspond to the formation of crystalline Fe3B, NdFe14B, and alpha-Fe, respectively. With increase of Dy concentration, H-j(c) increases to a maximum value at about x = 0.1, and then reduces gradually. The enhancement of coercivity arises from the increase of the anisotropy field for the hard magnetic phase. The reduction of intrinsic coercivity H-j(c) is attributed to the emergence of alpha-Fe after annealing at the third peak and the reduction of the fraction of hard magnetic phase due to the Dy addition. In order to obtain the optimum magnetic properties, a special annealing method was used.