Abstract:We describe here a simple and low-cost method to prepare ultra-thin, homogeneous, and transferable films of pristine carbon nanotubes (CNTs). The highly efficient chemical vapor deposition (CVD) growth method involves silica supported catalysts and alcohol vapor as gaseous carbon source. By varying the amount of catalysts, the thickness of synthesized films can be easily tuned from 20 nm (sub-monolayer) to 150 nm in a controlled fashion. High-resolution transmission electron microscopy (HRTEM) revealed that the films are composed primarily of single-walled and a small fraction of double-walled CNTs. A nonlinear relationship between film conductivity and thickness was observed. Our sub-monolayer (similar to 20 nm) film, which is noticeably thinner than conductive CNT films synthesized using other methods (typically > 50 nm and up to similar to 100 mu m), shows the highest conductivity of 400 mho . cm(-1) with similar to 90% transparency in the visible range and close to 100% transparency in the infrared range. This ultra-thin film can also be transferred carrier-film free to a wide range of substrates including low-cost plastics for flexible electronics. Compared to CNT films prepared by filtration techniques, our films demonstrated superior stability against mechanical bending.

Growth of Aligned Carbon Nanotubes on Self-Similar Macroscopic Templates

Synthesis of vertically aligned boron nitride nanotubes with a template of single-walled carbon nanotubes

Transferable thin films of pristine carbon nanotubes.

Uniform Patterned Growth of Carbon Nanotubes Without Surface Carbon

Lift-up Growth of Aligned Carbon Nanotube Patterns

Uniform Patterned Synthesis of Vertically-Aligned Carbon Nanotubes on Low-Stress Micromechanical Structures

Layered Growth of Aligned Carbon Nanotubes Arrays on Silicon Wafers

Electric-Field-Directed Growth of Aligned Single-Walled Carbon Nanotubes

Building and testing organized architectures of carbon nanotubes

Synthesis of Aligned Carbon Nanotubes by Thermal Chemical Vapor Deposition

Substrate-Site Selective Growth of Aligned Carbon Nanotubes

Growth of Well-Aligned Carbon Nanotube Arrays on Silicon Substrates Using Porous Alumina Film As a Nanotemplate

Multi-Directional Growth of Aligned Carbon Nanotubes Over Catalyst Film Prepared by Atomic Layer Deposition

Selective Growth of Carbon Nanotube on Silicon Substrates

Direction-Selective and Length-Tunable In-Plane Growth of Carbon Nanotubes

Template-confined growth and structural characterization of amorphous carbon nanotubes

Preferential Growth of Carbon Nanotubes/Nanofibers Using Lithographically Patterned Catalysts

Growth Of High-Quality Single-Wall Carbon Nanotubes Without Amorphous Carbon Formation

Rapid Growth of Well-Aligned Carbon Nanotube Arrays

Self-Aligned Growth and Optimization of Carbon Nanotube

Direct Growth of Three-Dimensional Multicomponent Micropatterns of Vertically Aligned Single-Walled Carbon Nanotubes Interposed with Their Multi-Walled Counterparts on Al-Activated Iron Substrates