Abstract:New Cu-based bulk glassy alloys were formed in Cu–Zr–Ti and Cu–Hf–Ti systems by the copper mold casting method. The critical diameter is 4 mm for the Cu60Zr30Ti10 and Cu60Hf25Ti15 alloys which are larger than 1 mm for the Cu60Zr40 and Cu60Hf40 glassy alloys. The substitution of Zr or Hf for Ti causes an increase in the glass-forming ability (GFA). As the Ti content increases, the glass transition temperature (Tg), crystallization temperature (Tx), and the supercooled liquid region ΔTx(=Tx−Tg) decrease for both Cu60Zr40−xTix and Cu60Hf40−xTix alloys. In contrast, the liquid temperature (Tl) has a minimum value of 1127 K for the Cu60Zr20Ti20 alloy and 1175 K for the Cu60Hf20Ti20 alloy, resulting in a maximum Tg/Tl of 0.63 and 0.62, respectively. The alloys with the highest Tg/Tl value showed the highest GFA for these Cu-based alloys. The bulk glassy alloys exhibit high tensile fracture strength of 2000–2160 MPa, compressive fracture strength of 2060–2150 MPa and compressive plastic elongations of 0.8–1.7%. The finding of the new Cu-based bulk glassy alloys with high GFA, high fracture strength above 2000 MPa and distinct plastic elongation is encouraging for the future development of a new type of bulk glassy alloy which can be used for structural materials.

Is Cu60Ti10Zr30 a Bulk Glass-Forming Alloy?

Bulk Nanostructure Formation Directly From The Multicomponent Alloy Melt

Glass-forming ability and differences in the crystallization behavior of ribbons and rods of Cu 36 Zr 48 Al 8 Ag 8 bulk glass-forming alloy

Zr-based Bulk Metallic Glass Composite with in Situ Precipitated Nanocrystals

Unusual Solidification Behavior of a Zr–Cu–Ni–Al Bulk Glassy Alloy Made from Low-Purity Zr

Glass-forming ability and differences in the crystallization behavior of ribbons and rods of Cu<sub>36</sub>Zr<sub>48</sub>Al<sub>8</sub>Ag<sub>8</sub>bulk glass-forming alloy

Formation and mechanical properties of Cu_(58)Zr_(20)Ti_(20)Mo_2 bulk metallic glass

High-strength Cu-based bulk glassy alloys in Cu–Zr–Ti and Cu–Hf–Ti ternary systems

Nanocrystalline Composites with High Strength Obtained in Zr–Ti–Ni–Cu–Al Bulk Amorphous Alloys

Failure behavior of Cu–Ti–Zr-based bulk metallic glass alloys

Cu-Based Bulk Glassy Alloys with Good Mechanical Properties in Cu-Zr-Hf-Ti System

Bulk metallic glass formation in the (Ti,Zr)-(Ni,Cu)-S system

Synthesis,structure and Mechanical Properties of Zr-Cu-based Bulk Metallic Glass Composites

Fabrication Of Bulk Glassy Hf50cu30ni10al10 Alloy By Copper Mold Casting

Homogeneity of the Superplastic Zr64.13Cu15.75Ni10.12Al10 Bulk Metallic Glass

A CuZr-based Bulk Metallic Glass Composite with Excellent Mechanical Properties by Optimizing Microstructure

Formation of A Phase Separating Bulk Metallic Glass in Cu40zr40al10ag10 Alloy

Bulk Glass Formation of 12 Mm Rod in La–Cu–Ni–Al Alloys

Formation and mechanical properties of bulk Cu-Ti-Zr-Ni metallic glasses with high glass forming ability

Pronounced Ductility in CuZrAl Ternary Bulk Metallic Glass Composites with Optimized Microstructure Through Melt Adjustment

Microstructure and Fracture Behavior of Zr55Cu30Al10Ni5 Bulk Metallic Glass and Its Composites Containing ZrO2