Preparation and thermoelectric properties of CuAlO2 compacts by tape casting followed by SPS
Liang Hao,Yan Zhang,Ryota Kubomura,Shingo Ozeki,Shiqi Liu,Hiroyuki Yoshida,Yingrong Jin,Yun Lu
DOI: https://doi.org/10.1016/j.jallcom.2020.157086
IF: 6.2
2021-02-01
Journal of Alloys and Compounds
Abstract:<p>We applied a novel method of tape casting followed by spark plasma sintering (SPS) to prepare CuAlO<sub>2</sub> compacts. During the tape casting process, plate-like Al<sub>2</sub>O<sub>3</sub> particles distributed along the flow direction of slurry under the action of the shear-thinning effect. It greatly elevated the orientation degree of the CuAlO<sub>2</sub> compacts formed during the following SPS. Meanwhile, the relative density of these compacts was also considerably increased due to the reduction in porosity. The green compacts and as-sintered compacts were characterized by X-ray diffraction (XRD) and scanning electron microscope (SEM). The thermoelectric properties including electrical resistivity, Seebeck coefficient, thermal conductivity, power factor, and the dimensionless figure of merit were measured. The results show that sample CuO-45-TC exhibited the highest thermoelectric performance with a <em>ZT</em> value of 0.042 at 973 K. The value should be the highest performance reported in the literature as far as we know. The remarkable increase in orientation degree and relative density should be responsible for the improvement in the thermoelectric performance of CuAlO<sub>2</sub>.</p>
materials science, multidisciplinary,chemistry, physical,metallurgy & metallurgical engineering