Microstructures and Thermoelectric Properties of Heusler Fe 2 VAl Alloys Containing Oxide Nanoparticles
Masashi Mikami,Kosuke Ogasawara,Hidetoshi Miyazaki,Yoichi Nishino
DOI: https://doi.org/10.2320/matertrans.mt-e2023003
2024-01-01
MATERIALS TRANSACTIONS
Abstract:The Heusler-type Fe2VAl alloy is a promising candidate for use in fabricating a thermoelectric power generation device because of its large Seebeck coefficient and high electrical conductivity. However, the high thermal conductivity of this alloy, as a thermoelectric material, degrades its power generation capacity. In this study, to reduce its thermal conductivity, the microstructure of a sintered Fe2V1.08Al0.92 alloy prepared via a powder metallurgical process was modified by adding oxide nanoparticles. Via the dispersion of Al2O3 nanoparticles, a sintered Fe2V1.08Al0.92 alloy with fine grains of approximately 200 nm in size was obtained due to the pinning effect on grain growth during sintering. The thermal conductivity was reduced from 16 to 11 W/mK. Upon La2O3 addition, the grain size of the Fe2V1.08Al0.92 alloy was reduced to approximately 100 nm and the thermal conductivity was further reduced to 10 W/mK. The difference in grain refinement could be caused by the lower stability of La2O3, which facilitated dispersion during ball milling, compared to that of Al2O3. As these microstructure refinements negatively affected the electronic properties, the thermoelectric performance of the Fe2V1.08Al0.92 alloy could not be enhanced. However, partial microstructure refinement with sparsely distributed La2O3 could slightly enhance the thermoelectric performance due to an appreciable reduction in the thermal conductivity without a considerable degradation in the electronic properties. By using these thermoelectric properties, a simple estimation of thermoelectric power generation, assuming a thermal resistance between the heat sources and thermoelectric module, was conducted. Remarkably, the results suggested that the reduction in thermal conductivity could enhance the output power density and conversion efficiency and reduce the optimal leg length. Thus, practically, controlling the balance between the electronic and thermal properties via microstructural modification is favorable in improving the practicability of the Fe2VAl alloy by enhancing the power generation capacity and reducing the sizes and masses of thermoelectric devices.
materials science, multidisciplinary,metallurgy & metallurgical engineering