Abstract:Abstract Because of the excellent fracture toughness and oxidation resistance, carbon short fiber reinforced ceramics have a sound potential for a variety of high‐temperature applications. For the composite's reliable use in long‐term applications, however, the oxidation effects on the mechanical strength are of crucial interest and have hitherto not been investigated in detail yet. In this study, the weight change of carbon short fiber reinforced C/SiC composites with carbon fiber lengths of 9 mm (long cut fiber composite – LCFC) and 2 mm (short milled fiber composite – SMFC), respectively, are evaluated in the temperature range from 500 to 1200 °C for two different fiber orientations. Both types of composites were additionally tested in bending mode after 25 and 50 min of exposure to air at 700 °C depending on fiber orientation. After 3 h of exposure at 1000 °C, a total weight loss of up to 37% for LCFC and 47% for SMFC could be determined. The bending test carried out after 50 min exposure at 700 °C showed a dramatic decrease down to 50% of the initial flexural strength for LCFC samples with fibers orientated in parallel to the beam axis. The smallest strength decrease of around 13% was found for SMFC samples with fibers orientated perpendicularly to the beam axis. Microstructural investigations suggest strongly that oxidation along the fibers is the most dominating weakening mechanism and is therefore directly affected by the fiber orientation and length.

Numerical Modeling of Oxidized C/SiC Microcomposite in Air Oxidizing Environments below 800 °C: Microstructure and Mechanical Behavior

A Progressive Oxidative Damage Model of C/SiC Composites under Stressed Oxidation Environments

Microstructure and oxidation behavior of SiOC coatings on C/C composites co-deposited with HMDS and TEOS by using CVD process

Failure Modeling of SiC/SiC Mini-Composites in Air Oxidizing Environments

The Degradation Behavior of C/Sic Composites in Complex Environment

Simulation of Mechanical Behaviors of Ceramic Composites Under Stress-Oxidation Environment While Considering the Effect of Matrix Cracks

The oxidation life analysis method for SiC/SiC composite components based on an equivalent diffusion coefficient model

Oxidation behaviors of carbon fiber reinforced multilayer SiC-Si3N4 matrix composites

Time-dependent matrix fracture of carbon fiber-reinforced silicon carbide ceramic-matrix composites considering interface oxidation

Non-Destruction Evaluation Method for Long-Term Oxidation Behavior of SiC/SiC Composites with Different Preforms in Wet Oxygen

An analytical model for the high temperature fracture strength of SiC fiber reinforced ceramic matrix composites considering oxidation and residual thermal stresses

Temperature-dependent oxidation kinetics and mechanical properties degradation of Cf/ZrB2-SiC composites

A Modified Iosipescu Method to Study In-Plane Shear Strength of C/SiC Composites at Elevated Temperatures in Air

Stress‐Oxidation Behavior of a Carbon/Silicon Carbide Composite in a High‐Temperature Combustion Environment

Oxidation behavior of 3D SiCf/SiBCN composites at 800–1200 °C

Influence of an O2 Type Oxidizing Environment on SiCf/SiC Composites: Properties/Microstructure Relationship

Oxidation Driven Damage on SiC/BN/SiC Ceramic Matrix Composite Aero-Engine Structures: An Iterative Computational Framework

Oxidation Kinetics and Its Impact on the Strength of Carbon Short Fiber Reinforced C/SiC Ceramics

Influence of Oxidation Damages on Mechanical Properties of SiC/SiC Composite Using Domestic Hi-Nicalon Type SiC Fibers

Oxidation Behavior of SiC/SiC Composites in Air at High Temperature

The Influence of Environmental Temperature on the Passive Oxidation Process in the C/SiC Composite