Abstract:A cross-linked silica and polyvinyl alcohol (PVA) hybrid material was prepared via a sol–gel process for use as a highly transparent, thermostable and mechanically strong coating. The effect of the H2O/TEOS ratio on the properties of the silica/PVA hybrid films, such as transmittance, thermal stability, mechanical strength, adhesive strength and hygrothermal resistance, is discussed herein. A strong chemical interaction between PVA and silica is indicated by the weakening of the C–OH peak and the formation of a Si–O–C peak in the XPS results. This interaction is further confirmed by the decrease in the PVA crystallinity from 23.29% to 2.56%, and the reduction in the silica/PVA melting point from 204.3 °C to 122.0 °C. This excellent compatibility between PVA and silica makes silica/PVA disperse well in solution with a dendritic-like or spherical morphology, and leads to a 97% increase in visible light transmittance. Therefore, compared with pure PVA, the obtained silica/PVA hybrid films are transparent. Even though the mass percentage of silica in the material is beyond 50 wt%, its Young's modulus is much improved from 0.17 ± 0.03 GPa to 2.52 ± 0.10 GPa, its ultimate tensile strength is enhanced from 40.1 ± 9.27 MPa to 80.3 ± 2.5 MPa, and its adhesive strength is increased from 475 N (1.52 MPa) to 712 ± 90 N (2.29 MPa) and it can almost maintain super hygrothermal resistance after 15 hygrothermal aging cycles. It is believed that the obtained silica/PVA hybrid could be used as a high-performance coating with excellent transparency, thermostability and mechanical strength.

Mechanical Properties of Low K SiO2 Thin Films Templated by PVA

Preparation Of Low-K Nanoporous Sio2 Films By Plasma-Enhanced Chemical Vapor Deposition

Characterization of ultra-low k porous organosilica thin films

Temperature-mediated Structural Evolution of Vapor–phase Deposited Cyclosiloxane Polymer Thin Films for Enhanced Mechanical Properties and Thermal Conductivity

Preparation and Characterization of Ultralow-Dielectric-Constant Porous SiCOH Thin Films Using 1,2-Bis(triethoxysilyl)ethane, Triethoxymethylsilane, and a Copolymer Template

Preparation and Properties of Ultra Low K Porous Silica Films Modified by Trimethylchlorosilane (TMCS)

20-P-11 Pure-silica Zeolite Low-K Dielectric Thin Films by Spin-on Process

Microstructure, Optical, Electrical Properties, and Leakage Current Transport Mechanism of Sol–gel-Processed High-K HfO2 Gate Dielectrics

Thermal Stability of Ultralow k Carbon-Bridged Periodic Mesoporous Organosilica Film

Preparation and Dielectric Properties of Polyimide/silica Nanocomposite Films Prepared from Sol–gel and Blending Process

Silica/polyimide Hybrids and Their Dielectric Properties. I. Preparation with an Improved Sol–gel Process with Poly(amic Acid) As the Precursor

Mechanical Properties and Interface Characteristics of Nanoporous Low-K Materials.

Preparation of Ultra Low-κ Porous SiOCH Films from Ring-Type Siloxane with Unsaturated Hydrocarbon Side Chains by Spin-On Deposition

Pure Silica Zeolite Films as Low-k Dielectrics by Spin-On of Nanoparticle Suspensions

Characterization of PECVD ultralow dielectric constant porous SiOCH films using triethoxymethylsilane precursor and cinene porogen

New Approach for the Preparation of Nanoporous Polyorganosilicate Low-K Films

A silica/PVA adhesive hybrid material with high transparency, thermostability and mechanical strength

Low dielectric constant films deposited by PECVD using tetraethoxysilane and limonene as precursors

Preparation and Research of Hydrophobic PDMS/Nano-SiO2 Modified SiO2 Coating

Controllable Preparation Of Ultra-Low-Dielectric Nanoporous Silica Via Inorganic-Organic Hybrid Templates

Tween-80 based ultra low-k (ULK) mesoporous films