Abstract:The oxide layer formed by ultra‐high melt point oxides (ZrO2, HfO2) and SiO2 glassy melt is the key to the application of traditional thermal structural materials in extremely high‐temperature environment. However, the negative effect of ZrO2 and HfO2 phase transitions on the stability of oxide layer and rapid volatilization of low viscosity SiO2 melt limit its application in aerospace. In this study, the ablation behavior of Cf/(CrZrHfNbTa)C‒SiC high‐entropy composite was explored systematically via an air plasma ablation test, under a heat flux of 5 MW/m2 at temperatures up to 2450°C. The composite presents an outstanding ablation resistance, with linear and mass ablation rates of 0.9 μm/s and 1.82 mg/s, respectively. This impressive ablation resistance is attributed to the highly stable oxide protective layer formed in situ on the ablation surface, which comprises a solid skeleton of (Zr, Hf)6(Nb, Ta)2O17 combined with spherical particles and SiO2 glassy melt. The irregular particles provide a solid skeleton in the oxides protective layer, which increased stability of the oxide layer. Moreover, the spherical particles have a crystal structure similar to that of Ta2O5 and are uniformly distributed in SiO2 glassy melt, which hinder the flow of SiO2 glassy melt and enhance its viscosity to a certain degree. And it reduces the volatilization of SiO2. In summary, the stable oxide layer was formed by irregular particles oxide and the SiO2 glassy melt with certain viscosity, thereby resulting in the impressive ablation resistance of the composite. This study fills a gap in ablation research on the (CrZrHfNbTa)C system.

Synthesis and Ultra-High Temperature Ablation Behavior of a ZrC/Cr2AlC Composite

Ablation Performances of Multi-Phased C/C-Zrc-Sic Ultra-High Temperature Composites

Synthesis and Anti-ablation Properties of in Situ ZrC Modified Carbon/Carbon Composites

Oxidation and ablation behaviours of ZrC modified carbon/carbon composites

Ablation Behavior and Mechanism of C/C–ZrC–SiC Composites under an Oxyacetylene Torch at 3000°C

Long-term oxidation and ablation behavior of C<sub>f</sub>/ZrB<sub>2</sub>-SiC composites at 1500, 2000, and 2200C

Ablation behavior and mechanisms of Cf/(CrZrHfNbTa)C‒SiC high‐entropy composite at temperatures up to 2450°C

Oxidation And Ablation Resistance Of C-F/Zrc-Sic Ultra-High Temperature Composites

Ultra-high-temperature ablation behavior of SiC–ZrC–TiC modified carbon/carbon composites fabricated via reactive melt infiltration

Microstructure and High Temperature Anti-Ablation Behavior of Cr-modified ZrC Coating for SiC-coated Carbon/carbon Composites

Ablation Resistant C/C-HfC-ZrC-TaC-SiC Composites Prepared by Reactive Melt Infiltration

Preparation and Ablation Behavior Analysis of Non-Equimolar C F /(hf 1/2 Zr 1/ 3 Ti 1/6 )C Composites under Oxyacetylene Flame with Different Heat Fluxes

Ablative and Mechanical Properties of C/C–ZrC Composites Prepared by Precursor Infiltration and Pyrolysis Process

Effect of Carbide Particles on the Ablation Properties of Tungsten Composites

Ablation behavior and mechanisms of 3D C<sub>f</sub>/ZrB<sub>2</sub>-SiC composite applied in long-term temperature up to 2400 C

Ablation resistance of ZrB2–SiC–AlN ceramic composites

Ablation behavior and mechanisms of 3D Cf/ZrB2-SiC composite applied in long-term temperature up to 2400 °C

Preparation and flame ablation/oxidation behavior of ZrB2/SiC ultra-high temperature ceramic composites

Preparation and ablation behavior analysis of non-equimolar Cf/(Hf1/2Zr1/3Ti1/6)C composites under oxyacetylene flame with different heat fluxes

Microstructure and ablation behavior of C/C composites doped with ZrB2

Ablation Behavior and Mechanism of C/C-ZrC Composites under Oxyacetylene Torch Flame