Abstract:Modulation of Si–O bonds in silica to achieve plastic deformation using supercritical CO2 under mild temperature is reported. Experimental and theoretical investigations suggest that CO2 molecules not only can promote the condensation of –Si–OH but also can intercalate into the microchannels of silica and induce the local strain of siloxane rings and facilitate the Si–O bond cleavage. Modulation of Si–O bonds under mild conditions has been a challenging issue in the field of material science, which is critical to manufacture high‐performance silica‐based optical and photonic devices. Herein, we introduce a nondestructive technique to achieve Si–O bond rearrangement, leading to plastic deformation and photoluminescence enhancement of amorphous silica nanoparticles using supercritical carbon dioxides in EtOH/H2O solution under mild temperature. Specifically, plastic deformation is achieved by treating hollow mesoporous silica nanospheres using supercritical CO2 at 40 °C under 20 MPa. Experimental and theoretical studies revealed the critical role of supercritical CO2 in the plastic deformation process, which can be intercalated into the hollow mesoporous silica nanospheres with anisotropic stresses and induces the rearrangement of Si–O bonds and transformation of ring structures. This work suggests a novel approach to engineer high‐performance nano‐silica glass components for numerous optical and photonic devices under mild condition.

Synthesis of Coesite Nanocrystals from Ethane Bridged Periodic Mesoporous Organosilica at Low Temperature and Extreme Pressure

Synthesis of Nano-Polycrystalline Coesite under High Temperature and High Pressure

Direct Formation of Mesoporous Coesite Single Crystals from Periodic Mesoporous Silica at Extreme Pressure.

Synthesis Of Periodic Mesoporous Coesite

Synthesis of mesoporous silica hollow spheres in supercritical CO2/water systems

On the High-Pressure Behavior of Periodic Mesoscale SBA-16 Silica/carbon Composites: Studies at 10 GPa Between 25 and 1800 °C

Investigation of High-Pressure and Temperature Behavior of Surfactant-Containing Periodic Mesostructured Silicas

Large-pore periodic mesoporous silicas with crystalline channel walls and exceptional hydrothermal stability synthesized by a general high-pressure nanocasting route

Structural Characteristics and Elasticities of Coesite and Coesite-Ii at High Pressure

Synthesis of Ordered Cubic Periodic Mesoporous Organosilicas with Ultra-Large Pores

Pressure-induced Structural Modulations in Coesite

Synthesis of Stishovite Nanocrystals from Periodic Mesoporous Silica.

Synthesis of siliceous hollow spheres with large mesopore wall structure by supercritical CO2-in-water interface templating.

Crystallization Behavior of Amorphous Si2bc3n Ceramic Monolith Subjected to High Pressure

Studies on the nanocrystalline Co3O4 by wet synthesis and its microstructure

Periodic Mesoporous Organosilica Nanocubes with Ultrahigh Surface Areas for Efficient CO2 Adsorption

Multiple Pathways in Pressure-Induced Phase Transition of Coesite.

Some IR features of SiO4 and OH in coesite, and its amorphization and dehydration at ambient pressure

Structural evolution of CO2 filled pure silica LTA zeolite under high-pressure high-temperature conditions

Melting and Subsolidus Relations of SiO2 at 9–14 GPa

CO2‐Induced Modulation of Si–O Bonds for Low Temperature Plastic Deformation of Amorphous Silica Nanoparticles with Enhanced Photoluminescence