Abstract:The transformation-assisted consolidation under pressure has been demonstrated to be a promising method to fabricate the nano or submicron polycrystalline ceramic materials. The high pressure suppresses the long-range diffusion of the atoms and, consequently, restrains the grain coarsening. The new phases produced at high pressure could show finer grains under the appropriate thermodynamic conditions, which are not subject to the grain size of the raw materials. Ceramic materials exhibit the existence of the transformations under certain thermodynamic conditions and the formation of new phases generally undergoes the nucleation and growth. In the present work, monoclinic microcrystal ZrO2 with average grain size of 2 µm and Y2O3 with average grain size of 50 nm were mixed in molar ratio of 97∶3. The preparation of the samples was carried out by sintering at 5.5 GPa and temperatures of 800–1700 °C using the high pressure cubic cell, and the sample characterization was performed via the X-ray diffraction, scanning electron microscope and transmission electron microscopy. It was found that the monoclinic and submicron tetragonal composite polycrystalline ZrO2 in bulk is obtained under high pressure and high temperature. The average grain size of tetragonal ZrO2 fabricated at 1200, 1400, 1600 and 1700 °C is (145±62) nm, (246±165) nm, (183±62) nm and (245±107) nm, respectively. The synthesis of the fine-grained polycrystalline materials by the transformation under high pressure can solve the problems of agglomeration, adsorption and grain coarsening caused by the nanopowders as the starting materials in the conventional approach, which would be an alternative route to fabricate the fine-grained polycrystalline materials with the enhanced performances.

Synthesis of Nano-Polycrystalline Coesite under High Temperature and High Pressure

Synthesis of Nano-Polycrystalline Diamond under High Pressure and High Temperature

Fabrication of Submicron Tetragonal Polycrystalline ZrO2 by the Transformation of Micro Monoclinic ZrO2 under High Pressure

High-pressure Synthesis of High-Performance Submicron-Sized Polycrystalline Β-Si3n4 Bulk Without Additives

Synthesis of Coesite Nanocrystals from Ethane Bridged Periodic Mesoporous Organosilica at Low Temperature and Extreme Pressure

Studies on the nanocrystalline Co3O4 by wet synthesis and its microstructure

Minicrystal And Xps Analysis Of Sio2 Coated Superfine Caco3 Powder

Nano-polycrystalline diamond formation under ultra-high pressure

Structural Characteristics and Elasticities of Coesite and Coesite-Ii at High Pressure

Polymorphic phase transition mechanism of compressed coesite

Crystal Structures and High-Temperature Vibrational Spectra for Synthetic Boron and Aluminum Doped Hydrous Coesite

Pressure-induced Structural Modulations in Coesite

Multiple Pathways in Pressure-Induced Phase Transition of Coesite.

Crystallization Behavior of Amorphous Si2bc3n Ceramic Monolith Subjected to High Pressure

Direct Formation of Mesoporous Coesite Single Crystals from Periodic Mesoporous Silica at Extreme Pressure.

Wurtzite-to-Rocksalt Structural Transformation in Nanocrystalline CoO

Bulk Modulus and Structural Phase Transitions of Wurtzite CoO Nanocrystals

In Situ Phase Transition Study of Nano- and Coarse-Grained Tio(2) under High Pressure/Temperature Conditions

Synthesis Of Periodic Mesoporous Coesite

In-situ Observation of Single-Phase Compositionally-Complex Oxide Formation During High-Pressure and High-Temperature Synthesis

Diamond Synthesis from a System of Chromium-Carbide and Ni 70 Mn 25 Co 5 Alloy