Optical and magnetic properties of nitrogen ion implanted MgO single crystal

Liu Chun-Ming,Gu Hai-Quan,Xia Xiang,Yan Zhang,Yong Jiang,Meng Chen,Zu Xiao-Tao,刘春明,顾海权,向霞,张焱,蒋勇,陈猛,祖小涛
DOI: https://doi.org/10.1088/1674-1056/20/4/047505
2011-01-01
Chinese Physics B
Abstract:The microstructure, optical property and magnetism of nitrogen ion implanted single MgO crystals are studied. A parallel investigation is also performed in an iron ion implanted single MgO sample as a reference. Large structural, optical and magnetic differences are obtained between the nitrogen and iron implanted samples. Room temperature ferromagnetism with a fairly large coercivity field of 300 Oe (1 Oe=79.5775 A/m), a remanence of 38% and a slightly changed optical absorption is obtained in the sample implanted using nitrogen with a dose of 1 x 10(18) ions/cm(2). Transition metal contamination and defects induced magnetism can be excluded when compared with those of the iron ion implanted sample, and the nitrogen doping is considered to be the main origin of ferromagnetism.
What problem does this paper attempt to address?