Understanding the recrystallization and phase transformation of gradient nanostructured M50 steel under the athermal effect of electrical pulses
Xiong Yue,Qian Sun,Shan Hu,Fei Yin,Lin Hua
DOI: https://doi.org/10.1016/j.matchar.2023.113072
IF: 4.537
2023-06-09
Materials Characterization
Abstract:M50 steel is a commonly used material for aeroengine main shaft bearings. In this study, a gradient nanostructured M50 steel was fabricated by an efficient surface nanocrystallization method, i.e., ultrasonic shot peening (USP) technology. The recrystallization behavior and phase transformation of gradient nanostructured M50 steel under the athermal effect of electrical pulses were investigated. Compared with the USPed sample, the ferrite structure size was 32.5% smaller, and the structure size uniformity was 51.5% greater in the 0–50 μm region after USP treatment and electrical pulsing treatment (EPT) with 38 A/mm 2 –1 s. Athermally induced ferrite recrystallization by EPT accompanied with obvious precipitation of VC and Mo 2 C carbides, and decomposition of austenite occurred during ferrite structure coarsening. EPT has different responses to different depths of gradient M50 steel, and there is an optimal current density to achieve structure refinement in different depths. However, the coarse-grain tempered M50 steel did not undergo obvious ferrite structure refinement under the same EPT parameters. The results revealed that the EPT promoted static recrystallization of incompletely recrystallized structures after USP processing by activating the release of stored deformation energy. Static recrystallization under the athermal effect of EPT was achieved by promoting the migration of the subgrain boundary to absorb the surrounding dislocations and increase the misorientation between itself and the surrounding ferrite structure. The mechanism of the athermal effect of EPT was based on electron-defect interactions, such as dislocations and lattice distortions. High-density nonequilibrium grain boundaries, acting as "active sites", accelerating the process of recrystallization under the effect of electric pulses. This study proposed a method for optimizing EPT parameters through the change in instantaneous resistance to evaluate the degree of recrystallization of the gradient structure.
materials science, multidisciplinary,metallurgy & metallurgical engineering, characterization & testing