Acceleration of Spheroidization in Low‐Density Ultrafine Pearlitic Steel by κ‐Carbide

Ming Chen,Chen Zhang,Guohong Zhang,Jie Zhou,Feng Hu,Kaiming Wu

DOI: https://doi.org/10.1002/srin.202300564

IF: 2.1258

2024-01-15

steel research international

Abstract:In this article, by adding 5% mass fraction aluminum to pearlite steel and annealing in different ways to form κ‐carbide, it is found that the carbide can significantly refine the lamellae spacing of low‐density ultrafine pearlite, and accelerate the spheroidization of low‐density ultrafine pearlite during the annealing process. The impact of κ‐carbide on the spheroidization process of low‐density ultrafine pearlitic steel (with 5 wt% Al and 5 wt% Mn additions) is investigated through isothermal annealing spheroidization. In the findings, it is demonstrated that κ‐carbides can significantly refine the lamellar spacing of low‐density ultrafine pearlite during the isothermal transformation. Additionally, under identical conditions, κ‐pearlite exhibits a higher number of ferrite/κ‐carbide interfaces. In the first stage of pearlite spheroidization, an abundance of dislocations and sub‐grain boundaries facilitate rapid fusion of the lamellar pearlite, while in the second stage, they provide a high‐speed diffusion pathway for carbon diffusion. Moreover, the reduced lamellar spacing shortens the distance for carbon and alloying elements diffusion, thereby promoting granular κ‐carbide formation and accelerating spheroidization in low‐density ultra‐fine pearlite.

metallurgy & metallurgical engineering