Ablation-resistance of ZrB2-SiC Coating under Oxygen-propane Torch Flame Prepared by Atmospheric Plasma Spraying
WANG Jia-wen,LIU Min,DENG Chun-ming,MAO Jie,HAN Wei,ZENG De-chang
DOI: https://doi.org/10.11933/j.issn.1007-9289.2016.04.013
2016-01-01
China surface engineering
Abstract:To improve the ablation resistance of C/C composites, ZrB2-SiC composite coatings were deposited on C/C composites by atmospheric plasma spraying (APS) process. Ablation tests were carried out on the ZrB2-SiC coated C/C composites using Oxygen-propane torch. The microstructures and phases of the coatings were analyzed by XRD, SEM and EDS. The results show that uniform and dense ZrB2-SiC composite coatings can be fabricated on the C/C composites by atmospheric plasma spraying (APS). After ablation at 1 600, 1 700 and 1 800 °C for 300 s, the weight of ZrB2-SiC coated C/C composites increases by 0.63%, 0.76% and 0.71%, respectively. While after ablation at 1 600, 1 700 and 1 800 °C for 600 s, the mass ablative rate of the coated specimen is 9.42×10, 2.04×10 and 1.04×10 g/s, respectively. The ZrB2-SiC composite coatings effectively enhance the ablation-resistance of C/C composites, and the oxidation product SiO2 can fill in the pores in the coatings. However, after the exhaustion of SiO2, the pores in the coating became the channels of the oxygen diffused into the C/C substrate, resulting in the failure of C/C substrate.