Abstract:The microstructure and structure of a Super304H superheater steel pipe after 47,000 h were analyzed by metallographic microscope, scanning electron microscope (SEM), and EDS, and its mechanical properties were measured by hardness meter. The results show that the austenitic grains appear on the outer wall of Super304H steel pipe after service, while the SEM and metallographic microscope tests show that the outer wall particles are coarse. There is an obvious corrosion layer on the outer surface, and the thickness of the corrosion layer on the windward surface is significantly higher than that on the leeward surface. The inner surface is refined and the hardness of the material is significantly increased; the outer surface, the inner surface, and the center all grow abnormally. In this case, the room temperature tensile strength and impact performance of the rough crystal area of the outer wall of the Super304H steel pipe are reduced and fracture along the crystal. Supervision should be strengthened to eliminate the safety risks caused by the abnormal growth of the outer wall austenite grain. The results of crystal phase microscopy show that the main structure of the material still maintains the basic structure of austenitic steel, and particle aggregation mainly occurs in the sub-inner layer of the inner and outer surface. Compared with the lee surface, the middle body structure is basically the same, but whether the thickness of the corrosion layer on the inner surface or the outer surface increases, the deformation degree of the deformation layer is greater. The hardness measurement finds that the hardness of the corrosion layer is caused by the increase in Super304H steel surface stress. In case of pipe explosion accident, the highest chance of pipe explosion here should be closely observed.

Intergranular corrosion susceptibility of a novel Super304H stainless steel

Revealing the Effect of O2, SO2 and H2O in Supercritical CO2 on the Corrosion Behavior of 316L Steel at Elevated Temperature

High-temperature corrosion data and mechanisms for T122, Super304H and HR3C after 15 years in 1000MW ultra-supercritical power plant

Microstructure Evolution of Super304H Steel Used in a Service Power Station Boiler

The Stress Corrosion Cracking of Austenitic Stainless Steel Heat Exchange Tubes: Three Cases Study

Research Progress on High-temperature Oxidation of Austenitic Stainless Steel for Ultra-superCritical Boilers

Intergranular precipitation behavior and its influence on the stress relaxation cracking susceptibility of Super304H austenitic stainless steel weld metal during long-term aging

Microstructural Evolution and Oxidation Resistance of T92 Boiler Tube Steel Upon Long-Term Supercritical Steam Test

Analysis and Solution of High-temperature Corrosion for a 1000 MW Ultra-supercritical Boiler

Failure analysis of a 304 stainless steel heat exchanger in liquid sulfur recovery units

Fireside Corrosion Behaviors Of Super304h And Hr3c In Coal Ash/Gas Environment With Different So2 Contents At 650 Degrees C

Fireside Corrosion Behaviors of Super304H and HR3C in Coal Ash/Gas Environment with Different SO 2 Contents at 650 °C

CORROSION PROPERTIES OF TP316L STEEL UNDER GASEOUS-PHASE CONDITION IN SUPERHEATER AREA OF BIOMASS-BURNING BOILERS

Research Progress of HR3C Heat Resistant Steel Used in Ultra Supercritical Boiler

Comparison and mechanism research of corrosion behavior of materials used in supercritical water-cooled reactors

Failure analysis of reheater tubes in a 350 MW supercritical circulating fluidized bed boiler

CORROSIVE CHARACTORS OF TP347H STEEL IN SUPERHEATER 'S ATMOSPHERE OF BIOMASS-BURNED BOILER

Development of weld filler material to match the advanced martensitic heat resistance steel G115 and tailoring the performance by tempering temperature

The Failure Mechanism of the 316 SS Heat Exchanger Tube in the Geothermal Water Environment

Experimental Investigation of Corrosion Associated with Gaseous HCl in the Superheaters in a Biomass Boiler

Corrosion Behavior of Superalloys in High Temperature Gas Cooled Reactor in Impure Helium with Corrosion Time