Abstract:Y2O3 nanomaterials have been widely used in transparent ceramics and luminescent devices. Recently there are many studies focusing on controlling the size and morphology of Y2O3 in order to obtain better materials performance. In present study, yttrium oxyhydroxide precursor was synthesized via a facile solvothermal process through the dissolution-recrystallization mechanism of Y2O3 raw powders in the ethylenediamine solvent, then nanosized yttrium oxide crystal was prepared from the precursor through post heat treatment process. The effects of solvothermal treatment temperature, holding time, solvent kinds and post heat treatment parameters on crystalline structure, grain shape and size of nanocrystal were investigated by XRD, TEM and TGA-DTA measurements. TEM images reveal that the morphology of product after post heat treatment at 460 °C for 12 h is rice-like nanocrystal. XRD shows that this product is pure cubic Y2O3 cphase. Present study reveals that high purity Y2O3 with rice-like morphology can be easily prepared with average size around 30 nm under suitable post heat treatment parameters. In addition the effects of solvents such as water and ethanol etc. on the crystal structure and morphology were also investigated. It is suggested that dissolution-recrystallization process may be the main mechanism for the formation of nano-sized YOOH precursors under solvothermal reaction condition, and the ethylenediamine solvent is likely to play an important role in controlling the transformation process of yttria precursors to the Y2O3 nanocrystal.

Influence of the Synthesis Conditions on Preparation of Yttria Powders by Urea Precipitation Method

Study on Preparation of Yttrium Oxide with Large Particle Sizes and Spherical Shapes by Precipitation with Ammonium Bicarbonate

Preparation and Spherical Morphology Control of Γ-La_2s_3 Powders by Homogeneous Precipitation

Yttria Nanopowders with Low Degree of Aggregation by a Spray Precipitation Method

Yttria Nanopowders Manufactured by the Combustion Synthesis Process of Yttrium Citrate-Urea

Monodispersed Spherical Y2O3 and Y2O3:Eu3+ Particles Synthesized from Modified Homogeneous Urea Precipitation Process

Effect of synthesis conditions on the performance of weakly agglomerated nanocrystalline NiO

Influences of Preparation Conditions on the Ytterbium-Doped Tin Oxide Nano-Powders

Orthogonal Experimental Optimization for Preparation Ofyag Nano-Powders by Co-Precipitation Method

Preparation of YAG Nanopowder by Hydrothermal- Homogeneous Precipitation Method

Preparation and characterization of nano-scale Y2O3-ZrO2 powder by heterogeneous precipitation

Comparative Study of Synthesis and Characterization of YAG:Yb3+ Nanoparticles Using Different Precipitator by Co-Precipitation Method

Preparation of nano-sized Y_2O_3 by ammonium oxalate precipitation method

Preparation of YAG Nano-sized Powders Dependent on Different Precipitating Agents

Preparation of ultra-fine yttrium oxide by ultrasonic-quenching-homogeneous precipitation method

Nanoscaled YAG Powders Via Coprecipitation Using Ammonium Hydrogen Carbonate As the Precipitant

Effect of Ammonium Sulfate on the Monodispersed Y3Al5O12 Nanopowders Synthesized by Co-Precipitant Method

Formation Mechanism of Impure Phases and Crystallinity Investigation of YAG Powders Synthesized Via the Co-precipitation Method

Synthesis of Yttrium Oxide Nanocrystal Via Solvothermal Process

Synthesis of nanoscaled yttrium aluminum garnet powder by the co-precipitation method

INFLUENCE OF REACTION CONDITIONS ON PREPARATION OF Nd:YAG POWDERS AND TRANSPARENT CERAMICS BY HOMOGENEOUS PRECIPITATION METHOD