Abstract:Employing HNO3, NH3· H2O, NH4NO3, H2C2O4 and commercial available Y2O3 as starting materials, and using SDBS as surfactant and PEG 2000 as assistant , the precursor Y ( NH4 ) ( C2 O4 ) 2· H2 O and its final products Y 2 O3 powders were successfully fabricated by the improved oxalate precipitation method and subsequent calcination treatment .In this specific route , a little amount of designed Y(NO3)3 solution was added into a certain huge volume of NH 3· H2O-NH4NO3 mixed solution to create Y(OH)3 hydro-gel, so the pH value could be precisely controlled during the process .Then the precursor precipitate was produced by dropping the saturated oxalate acid solution into the obtained white colloidal at 85 ℃.At last, following heat treatment at 950 ℃ for 2 h, the final product Y2 O3 powders were obtained .X-ray powder diffraction ( XRD) and scanning electron microscopy ( SEM) results revealed that the pre-cursor Y(NH4)(C2O4)2· H2O in forms of cubic crystal aggregations was obtained .Despite substantial removal of oxide, carbon and hydrogen ions , the precursor calcined Y 2 O3 particles maintained well morphology properties of the precursor even after calcination at 950 ℃for 2 h.Further, to understand the factors influencing the size and morphology of the final Y 2 O3 particles, experiments were carried out by mainly changing the mass ratio of SDBS/PEG2000 and the pH value in the oxalate acid precipitation process .It was ob-served from the SEM results that the size and shape of the synthesized Y 2 O3 particles could be controlled by precisely adjusting reaction conditions, especially the pH value in the oxalate acid precipitation process .Y2 O3 particles with diameter under 1μm could be made when the pH value in the oxalate acid precipitation process was reduced to 1.8.In addition, based on the thermogravimetric (TG) and differential scanning calorimetry ( DSC) analysis, the thermal decomposition mechanism of precursor was proposed as follows: Y (NH4)(C2O4)2· H2O→Y(NH4)(C2O4)2→Y2O2CO3→Y2O3.

Preparation of ultra-fine yttrium oxide by ultrasonic-quenching-homogeneous precipitation method

Study on Preparation of Yttrium Oxide with Large Particle Sizes and Spherical Shapes by Precipitation with Ammonium Bicarbonate

Preparation of nano-sized Y_2O_3 by ammonium oxalate precipitation method

Preparation and characterization of nano-scale Y2O3-ZrO2 powder by heterogeneous precipitation

Preparation of Ultrafine Yttria by Wet-Solid-Phase Mechanochemical Reaction

Synthesis of Yttrium Oxide Nanocrystal Via Solvothermal Process

Preparation of nano-sized lanthanum oxide by ultrasonic-homogeneous precipitation method

Size-and Shape-Controlled Synthesis and Formation Mechanism of Y(NH4)(C2O4)2·H2O and Y2O3 Phases

Preparation of Ultrafine Α-Al2o3 Powder by Homogenous Precipitation

Synthesis of Y2O3 nanopowders and transparent Y2O3 ceramics by carbonate-precipitation process

Preparation And Characterization Of Nano-Yb2o3/Tio2 Particles

A Novel Route for the Preparation of Ultrafine Yttria-Doped Zirconia Powders

Preparation and Characterization of Monodispersed Spherical Eu2O3 Ultrafine Particles

Ultrasonic Spray Co-Precipitation for YAG Nano-Powders Preparation

Orthogonal Experimental Optimization for Preparation Ofyag Nano-Powders by Co-Precipitation Method

Preparation of Ultrafine Cobalt Oxide Powder Precursor by Oxalate Precipitation

Co-precipitation of nano Mg–Y/ZrO2 ternary oxide eutectic system: Effects of calcination temperature

Preparation of Nanoscale Ytterbia by Wet Chemical Methods

Preparation of nano-ZnO by direct precipitation method under ultrasonic radiation and surface modification study

Preparation of YAG Nano-Powders Via an Ultrasonic Spray Co-Precipitation Method

Preparation of ultrafine zirconia powder by emulsion method