Abstract:Ni–W–Co alloy is a recently developed single-phase Ni-based alloy with high density. An ultra-high content of W (35–38 wt%) is essential to ensure the high density but unfavorable to possess outstanding ductility or present large deformation. In this study, the flow stress behavior and hot workability of Ni–W–Co alloy were investigated through simulated compression tests with a temperature range of 1000–1300 °C and strain rate range of 0.01–5 s −1 . The Arrhenius-type constitutive equation at peak stress was established. The constitutive equation displays prediction bias due to the lower experimental values at low temperature and high strain rate. The ultra-high solution content of W not only results in the severely inhibited discontinuous dynamic recrystallization (DDRX) and high apparent deformation activation energy (568.5 kJ/mol) but also promotes the generation of subgrain boundaries. Furthermore, continuous dynamic recrystallization (CDRX) occurs during deformation at a low temperature and a high strain rate, which is quite different from the Ni-based alloy with a low W content that only DDRX occurs. The activation of CDRX shortens the stage at which work hardening dominates, and results in lower peak stress values. The prediction bias of the constitutive equation caused by the lower peak stress was eliminated through difference compensation. The hot processing maps at strain values of 0.3, 0.5, 0.7, and 0.9 were constructed. The optimal hot processing parameters of the Ni–W–Co alloy, which aims to obtain full recrystallization microstructure without defects, are strain rate 0.01–0.1 s −1 and temperature 1225–1300 °C in combination with the hot processing maps and microstructure evolution. This study provides a reference for the hot processing and microstructural modification of the novel Ni–W–Co alloy with an ultra-high W content.

Preparation of W-Ni graded alloy by combustion synthesis melt-casting under ultra-high gravity

Refining Micron-Sized Grains to Nanoscale in Ni-Co Based Superalloy by Quasistatical Compressive Deformation at High Temperature

Effects of Super-gravity Field on Solidification Structure and Microhardness of Al-Ni-Cr Alloy

Influence of Co Contents and Super-Gravity Field on Refinement of In-Situ Ultra-Fined Fibers in Al-2.5Ni Eutectic Alloys

Fine-grained 93W-4.9Ni-2.1Fe alloy with ultrahigh yield strength prepared via low temperature sintering of W nanocomposite powder

High-gravity Combustion Synthesis of W-Cr Alloys with Improved Hardness

Microstructure and Microsegregation in A Ni-Based Single Crystal Superalloy Directionally Solidified under High Thermal Gradient

Preparation of Fe3Al Alloy by Combustion Synthesis Melt-Casting under Ultra-High Gravity

Grain-size gradient structure by abnormal grain growth

Fabrication of gradient WC-Ni cemented carbide materials by high gravity-assisted combustion synthesis and infiltration

The W alloying effect on thermal stability and hardening of nanostructured Cu-W alloyed thin films

Achieving Enhanced Strength Retention at Elevated Temperatures in Ultrafine-Fibrous Interconnected Al-Ce-Ni Eutectic Alloy Solidified under Super-Gravity Field

Preparation of WC/CoCrFeNiAl0.2 high-entropy-alloy composites by high-gravity combustion synthesis

Hot deformation behavior of a novel Ni–W–Co high-density Ni-based alloy with ultra-high W content

A novel dissolution-precipitation mechanism during liquid phase sintering and its strengthening effects in W-Ni-Fe alloys with low W contents

Combustion synthesis of porous TiC/Ni composites under high gravity

Microstructure and mechanical properties of TiC-Ni functionally graded materials by simultaneous combustion synthesis and compaction

Fabrication of Bulk Al2o3 by Combustion Synthesis Melt-Casting under Ultra-High Gravity

Fabrication and Characterization of Tungsten Heavy Alloys with High W Content by Powder Metallurgy

Achieving fine-grain tungsten heavy alloys by selecting a high entropy alloy matrix with low W grain growth rate

Fabrication of 60 wt%W-40 wt%Cu composite with crystal orientation by combustion synthesis and melt-infiltration in ultrahigh-gravity field