Abstract:Due to their anisotropic behavior, composite structures are weak in transverse direction loading. produces transverse cracks, which for a laminated composite, may lead to delamination and total failure. The transition from transverse crack to delamination failure is important and the subject of recent studies. In this paper, a simulation of transverse crack and its transition to delamination on cross-ply laminate was studied extensively using a cohesive element Finite Element Method (FEM). A pre-cracked [0/90] composite laminate made of bamboo was modeled using ABAQUS/CAE. The specimen was in a three-point bending configuration. Cohesive elements were inserted in the middle of the 90° layer and in the interface between the 0° and 90° layer to simulate transverse crack propagation and its transition to delamination. A load–displacement graph was extracted from the simulation and analyzed. As the loading was given to the specimen, stress occurred in the laminates, concentrating near the pre-cracked region. When the stress reached the tensile transverse strength of the bamboo, transverse crack propagation initiated, indicated by the failure of transverse cohesive elements. The crack then propagated towards the interface of the [0/90] laminates. Soon after the crack reached the interface, delamination propagated along the interface, represented by the failure of the longitudinal cohesive elements. The result of the numerical study in the form of load–displacement graph shows a consistent pattern compared with the data found in the literature. The graph showed a linear path as the load increased and the crack propagated until a point where there was a load-drop in the graph, which showed that the crack was unstable and propagated quickly before it turned into delamination between the 0o and 90° plies.

Snap-through of Bi-Stable Rectangular Unsymmetric Cross-Ply Composite Laminates

Study on a New Concept of Multi-Stable Lattice Structure

Prediction of Critical Center Load for Bi-Stable Laminates

Analytical Solution for Externally Bonded Joints Considering Snap-Back

Design and analysis of a tri-stable structure based on bi-stable laminates

On the Through-the-Width Multiple Delamination, and Buckling and Postbuckling Behaviors of Symmetric and Unsymmetric Composite Laminates

Bistable Characteristics of Unsymmetric Cross-ply Composite Laminates Considering Different Boundary Shapes

Numerical and Experimental Study on Morphing Bi-Stable Composite Laminates Actuated by A Heating Method

Numerical simulation and experiment validation of variable stiffness composite laminates with open holes under unidirectional tension

Computational modelling of postbuckling behavior of composite T-stiffened panels with different bonding methods

Static and Dynamic Symmetric Snap-Through of Non-Uniform Shallow Arch under a Pair of End Moments Considering Critical Slowing-Down Effect

Exact analysis of postbuckling behavior of anisotropic composite slender beams subjected to axial compression

Three-dimensional Finite Element Analysis on Interlaminar Stresses of Symmetric Laminates

Local Buckling Prediction for Multiple-Delaminated Laminate Using the Critical Load of the Sub-Laminate Having the Maximum Flexural Stiffness

A multi-stable lattice structure and its snap-through behavior among multiple states

Multistable Morphing Structures Integrated with Non-Symmetric/Antisymmetric-Layup Connected Laminates

A numerical investigation on delamination buckling behavior in laminated composites under compressive load

Progressive Failure Analysis of Composite Laminates Subjected to Transverse Loading with Augmented Finite Element Method

Numerical Simulation of Transverse Crack on Composite Structure Using Cohesive Element

Nonlinear Stiffness Analysis of Thick Composite Laminate under Biaxial Load

Design and Analysis of Multistable Curvilinear-fiber Laminates Based on Continuous Fiber 3D Printing of Thermosetting Resin Matrix