Abstract:The augmented finite element method (A-FEM) is used to study the fundamental composite failure problem of delamination and associated damage events spreading from a stress concentrator during tensile loading. The solution exploits the ability of A-FEM to account for coupled multiple crack types that are not predetermined in shape or number. The nonlinear processes of each fracture mode are represented by a cohesive model, which provides a unified description of crack initiation and propagation and can also describe crack coalescence and bifurcation. The study problem is an orthogonal double-notched tension specimen, in which delaminations interact with transverse ply cracks, intra-ply splitting cracks, non-localized fine-scale matrix shear deformation, and fiber breaks. Cohesive laws and constitutive laws for matrix shear deformation are calibrated using literature data from independent tests. The calibrated simulations are mesh independent and correctly reproduce all qualitative aspects of the coupled damage evolution processes. They also correctly predict delamination sizes and shapes, the density of transverse ply cracks, the growth rate of splitting cracks, softening of the global stress–strain curve, and the ultimate strength. A sensitivity analysis relates variability in cohesive law parameters to predicted deviance in engineering properties. Given the known variability in cohesive law parameters, the predicted deviance in ultimate strength agrees with that in experimental data. The importance of including the interactions between different crack systems and non-localized shear deformation is demonstrated by suppressing the presence of separate mechanisms; the predicted delamination shapes, splitting crack growth rate, and the stress–displacement relationship fall into significant error.

Progressive fracture analysis of the open-hole composite laminates: experiment and simulation

Micro Failure Analysis of Fiber Metal Laminates

Damage Analysis of Composite Laminate with Large Open-hole under Compression Using 3D Strain Progressive Damage Theory

An Effective Progressive Damage Analysis Method for Failure Analysis of Composite Scarf Joint

Progressive Failure Analysis of Composite Laminates Subjected to Transverse Loading with Augmented Finite Element Method

Compressive Experiment and Damage Simulation of A Composite Structure with Ply Drop-Off

Progressive Damage Analysis and Experiments of Open-Hole Composite Laminates Subjected to Compression Loads

Tensile Progressive Damage and Compressive Postbuckling Analysis of Open-Hole Laminate Composites

Numerical Investigation on the Repeated Low-Velocity Impact Behavior of Composite Laminates

Finite Element Analysis of a Modified Progressive Damage Model for Composite Laminates under Low-Velocity Impact

Progressive Failure Analysis Of The Open-Hole Composites Laminates Using Sfem Method And Test Validation

Micromechanical Progressive Damage Analysis of Inter- and Intra-Layer Failures in Fiber-Reinforced Composite Laminates

Mechanical simulation of open hole compressive behavior for high-modulus and high-strength composite laminates

Strain Concentrations and Progressive Damage Analysis of Notched Composite Laminates

Numerical study on failure behavior of open-hole composite laminates based on LaRC criterion and extended finite element method

Progressive Damage Simulation of Open-Hole Composite Laminates under Compression Based on Different Failure Criteria

Progressive Damage Simulation of Scaling Effects on Open-Hole Composite Laminates under Compression

Finite Element Analysis of Progressive Failure and Strain Localization of Carbon Fiber/Epoxy Composite Laminates by ABAQUS

High-fidelity Simulations of Multiple Fracture Processes in a Laminated Composite in Tension

A Combined Experimental and Computational Analysis of Failure Mechanisms in Open-Hole Cross-ply Laminates under Flexural Loading

Progressive Damage Based Failure Analysis of Open-hole Composite Laminates under Tension