Abstract:This research aims at increasing the utilization of platinum-ruthenium alloy (Pt-Ru) catalysts and thus lowering the catalyst loading in anodes for methanol electrooxidation. The direct methanol fuel cell’s (DMFC) anodic catalysts, Pt-Ru/C, were prepared by chemical reduction with a reducing agent added in two kinds of solutions under different circumstances. The reducing agent was added in hot solution with the protection of inert gases or just air, and in cold solution with inert gases. The catalysts were treated at different temperatures. Their performance was tested by cyclic voltammetry and potentiostatic polarization by utilizing their inherent powder microelectrode in 0.5 mol/L CH3OH and 0.5 mol/LH2SO4 solution. The structures and micro-surface images of the catalysts were determined and observed by X-ray diffraction and transmission electron microscopy, respectively. The catalyst prepared in inert gases showed a better catalytic performance for methanol electrooxidation than that prepared in air. It resulted in a more homogeneous distribution of the Pt-Ru alloy in carbon. Its size is small, only about 4.5 nm. The catalytic performance is affected by the order of the reducing agent added. The performance of the catalyst prepared by adding the reductant at constant temperature of the solution is better than that prepared by adding it in the solution at 0°C and then heating it up to the reducing temperature. The structure of the catalyst was modified, and there was an increase in the conversion of ruthenium into the alloyed state and an increase in particle size with the ascension of heat treatment temperature. In addition, the stability of the catalyst was improved after heat treatment.

Effects of Sputtering Parameters on the Performance of Sputtered Cathodes for Direct Methanol Fuel Cells

Direct Methanol Fuel Cells: the Effect of Electrode Fabrication Procedure on Meas Structural Properties and Cell Performance

Fabrication of High-Performance Gas Diffusion Electrode Via Microporous Layer Surface Morphology Control

Effect of cathode gas flow patterns on performance of micro direct methanol fuel cell

Effect of the Microporous Layer Structure and Hydrophobicity on the Performance of Direct Methanol Fuel Cells

Platinum/carbon Intergated Electrodes for Direct Methanol Fuel Cells

Effects Of The Nanoimprint Pattern On The Performance Of A Mems-Based Micro Direct Methanol Fuel Cell

Technical advances in membrane electrode assembly fabrication for direct methanol fuel cell

A Liquid–Vapor Two-Phase Model of Direct Methanol Fuel Cells With Platinum Group Metal-Free Cathode Catalyst

Membrane Electrode Assembly with Ultra Low Platinum Loading for Cathode Electrode of PEM Fuel Cell by Using Sputter Deposition

Effects of Microporous Layer Preparation on the Performance of an Air-Breathing Direct Methanol Fuel Cell

Improvement of Direct Methanol Fuel Cell Performance by Modifying Catalyst Coated Membrane Structure

Effect of Different Structures of Carbon Supports for Cathode Catalyst on Performance of Direct Methanol Fuel Cell

Effects of MEA preparation on the performance of a direct methanol fuel cell

Comparative Studies of Configurations and Preparation Methods for Direct Methanol Fuel Cell Electrodes

Optimization of Membrane Electrode Assembly in Air-Breathing Direct Methanol Fuel Cell

Performance of Proton Exchange Membrane Fuel Cell Electrodes Prepared by Direct Deposition of Ultrathin Platinum on the Membrane Surface

Preparation and Influence of Performance of Anodic Catalysts for Direct Methanol Fuel Cell

High-performance anode for Polymer Electrolyte Membrane Fuel Cells by multiple-layer Pt sputter deposition

Effect of Operating Conditions on the Performance of a Direct Methanol Fuel Cell with PtRuMo/CNTs As Anode Catalyst

Preparation of High Active Pt/C Cathode Electrocatalyst for Direct Methanol Fuel Cell by Citrate-Stabilized Method